Metal nanoink and process for producing the metal nanoink, and die bonding method and die bonding apparatus using the metal nanoink
View Patent ↗Metal nanoink ( 100 ) for bonding an electrode of a semiconductor die and an electrode of a substrate and/or bonding an electrode of a semiconductor die and an electrode of another semiconductor die by sintering under pressure is produced by injecting oxygen into an organic solvent ( 105 ) in the form of oxygen nanobubbles ( 125 ) or oxygen bubbles ( 121 ) either before or after metal nanoparticles ( 101 ) whose surfaces are coated with a dispersant ( 102 ) are mixed into the organic solvent ( 105 ). Bumps are formed on the electrode of the semiconductor die and the electrode of the substrate by ejecting microdroplets of the metal nanoink ( 100 ) onto the electrodes, the semiconductor die is turned upside down and overlapped in alignment over the substrate, and then, the metal nanoparticles of the bumps are sintered under pressure by pressing and heating the bumps between the electrodes. As a result, generation of voids during sintering under pressure is minimized.
1. A metal nanoink comprising:
a dispersant comprising carbon;
a plurality of metal nanoparticles, each of the nanoparticles comprising a coating of the dispersant; and
an organic solvent comprising oxygen nanobubbles, the solvent comprising oxygen at a supersaturated concentration which is at least five times an oxygen saturation concentration in the organic solvent;
wherein oxygen is present only as dissolved oxygen and oxygen nanobubbles.
2. The metal nanoink of claim 1 , wherein each of the metal nanoparticles comprises an uncoated diameter of 5 to 50 nm.
3. The metal nanoink of claim 2 , wherein each of the metal nanoparticles comprises a coated diameter is substantially 100 nm.
4. The metal nanoink of claim 1 , wherein the plurality of metal nanoparticles is selected from the group of gold, silver, copper, platinum, palladium, nickel, and aluminum.
5. The metal nanoink of claim 1 , wherein the organic solvent may be a nonpolar solvent or a low polar solvent.
6. The metal nanoink of claim 1 , wherein the organic solvent has a boiling point greater than room temperature.
7. The metal nanoink of claim 1 , wherein the dispersant is selected from the group of an alkylamine, an alkanethiol, or an alkanediol.
8. The metal nanoink of claim 7 , wherein the plurality of metal nanoparticles is selected from the group of gold, silver, copper, platinum, palladium, nickel, and aluminum.
9. The metal nanoink of claim 8 , wherein the organic solvent is selected from the group of a terpineol, a mineral spirit, a xylene, a toluene, a tetradecane, or a dodecane solvent.
10. The metal nanoink of claim 9 , further comprising an organic binder.
11. The metal nanoink of claim 1 , wherein the oxygen nanobubbles comprise a diameter of substantially 100 nm.
12. A metal nanoink comprising:
a dispersant comprising carbon;
a plurality of metal nanoparticles, each of the nanoparticles comprising a coating of the dispersant; and
an organic solvent comprising oxygen nanobubbles, the solvent comprising oxygen at a supersaturated concentration which is at least five times an oxygen saturation concentration in the organic solvent;
wherein the dispersant, when heated to 150 degrees centigrade, comprises a fluidity less than gaseous carbon dioxide; and
wherein the organic solvent, when heated to 150 degrees centigrade, comprises a fluidity less than gaseous carbon dioxide.
13. A method of making metal nanoink, the method comprising:
(a) coating a plurality of metal nanoparticles with a dispersant to form a plurality of coated metal nanoparticles, the dispersant comprising carbon;
(b) mixing the plurality of coated metal nanoparticles with an organic solvent to form a mix; and
(c) injecting oxygen nanobubbles into the mix to create a supersaturated concentration of oxygen which is at least five times an oxygen saturation concentration in the organic solvent;
wherein oxygen is present only as dissolved oxygen and oxygen nanobubbles.
14. The method of claim 13 , wherein the dispersant, when heated to 150 degrees centigrade, comprises a fluidity less than gaseous carbon dioxide; and
wherein the organic solvent, when heated to 150 degrees centigrade, comprises a fluidity less than gaseous carbon dioxide.
15. The method of claim 13 , wherein step (b) is performed by mixing the plurality of coated metal nanoparticles into the organic solvent.
16. The method of claim 13 , wherein step (b) comprising adjusting a viscosity of the mix.
17. The method of claim 16 , wherein a viscosity of the mix is adjusted when the viscosity conforms to a shape of a predetermined ejection head.
18. The method of claim 13 , wherein step (c) is performed for at least 10 hours.
19. The method of claim 13 , wherein step (c) is performed using an injection nozzle held below a surface boundary of the mix.
20. The method of claim 13 , wherein step (c) is performed by shearing oxygen bubbles.
21. The method of claim 20 , wherein step (c) further includes detecting an oxygen concentration.
22. The method of claim 13 , wherein after step (b) and prior to step (c) the mix is transferred to a container, wherein oxygen bubbles that are larger than nanobubbles can vent to an ambient environment.