Method for reducing dielectric constant of film using direct plasma of hydrogen
A method for reducing a dielectric constant of a film includes (i) forming a dielectric film on a substrate; (ii) treating a surface of the film without film formation, and (III) curing the film. Step (i) includes providing a dielectric film containing a porous matrix and a porogen on a substrate, step (ii) includes, prior to or subsequent to step (iii), treating the dielectric film with charged species of hydrogen generated by capacitively-coupled plasma without film deposition to reduce a dielectric constant of the dielectric film, and step (iii) includes UV-curing the dielectric film to remove at least partially the porogen from the film.
1. A method for reducing a dielectric constant of a film, comprising (i) forming a dielectric film on a substrate; (ii) treating a surface of the film without film formation, and (III) curing the film, wherein:
step (i) comprises forming a dielectric film containing a porous matrix and a porogen on a substrate using capacitively-coupled electrodes,
step (ii) comprises, prior to step (iii), treating the dielectric film with charged species of hydrogen generated by plasma without film deposition so as to remove a porogen weakly coupled with a film matrix of the dielectric film and inhibit aggregation of a porogen in the film matrix, said plasma being generated using the capacitively-coupled electrodes, said charged species of hydrogen containing both excited hydrogen radicals and hydrogen ions, and
step (iii) comprises UV-curing the dielectric film to remove at least partially the porogen from the film.
2. The method according to claim 1 , wherein the charged species of hydrogen is comprised predominantly of excited hydrogen radicals and hydrogen ions.
3. The method according to claim 2 , wherein in step (ii), no species generated in a remote plasma unit are used for treating the dielectric film.
4. The method according to claim 2 , wherein the charged species of hydrogen is generated from a reducing gas containing hydrogen supplied over the dielectric film, to which hydrogen gas RF power is applied in-situ.
5. The method according to claim 4 , wherein the RF power is about 0.7 W/cm 2 or less per area of the substrate at a temperature of about 200° C. to about 250° C. under a pressure of about 20 Pa to about 200 Pa.
6. The method according to claim 5 , wherein the reducing gas is hydrogen gas.
7. The method according to claim 1 , wherein step (i) and step (ii) are continuously conducted without breaking vacuum.
8. The method according to claim 1 , wherein the dielectric film has a thickness of 200 nm or more prior to steps (ii) and (iii).
9. The method according to claim 1 , wherein the step of providing the dielectric film containing the porous matrix and the porogen comprises supplying a porogen gas and a precursor gas at a ratio of about 2 to about 6 of porogen gas flow to precursor gas flow, and depositing a film on the substrate by plasma CVD.
10. The method according to claim 9 , wherein the precursor gas comprises a silicon-containing gas, and the porogen gas comprises a hydrocarbon gas.
11. The method according to claim 1 , wherein the step of treating the dielectric film with charged species of hydrogen generated by capacitively-coupled plasma is the only step in step (ii).
12. The method according to claim 1 , wherein after steps (i) to (iii), the dielectric film has a dielectric constant of 2.15 or lower.
13. The method according to claim 1 , wherein a dielectric constant of the dielectric film is decreased by at least 0.1 as a result of conducting step (ii).
14. The method according to claim 1 , wherein an elastic modulus of the dielectric film remains substantially unchanged as a result of conducting step (ii).
15. The method according to claim 1 , wherein step (i) and step (ii) are conducted in the same reaction chamber.
16. The method according to claim 9 , wherein a distance between electrodes for generating the plasma in step (ii) is greater than that in step (i).