Nickel-iron alloy plating solution
View Patent ↗A nickel-iron alloy plating solution which can suppress, in a nickel-iron alloy plating solution containing divalent iron ions and divalent nickel ions, oxidation of divalent iron ions to trivalent iron ions and can prevent the occurrence of the precipitation of iron (III) hydroxide to allow stable continuous operation and also to provide a nickel-iron alloy plating solution which allows production of a soft magnetic film which is stable in composition. The nickel-iron alloy plating solution of the present invention is characterized in that it comprises divalent iron ions, divalent nickel ions and a hydroxylamine salt and has a pH of 3.0 or lower.
1. A nickel-iron alloy plating solution comprising divalent iron ions, divalent nickel ions and a hydroxylamine salt and having a pH of no more than 3.0, wherein the concentration of the hydroxylamine salt is 1/100 to 1/2 as a molar ratio to that of the divalent iron ions, the concentration of the divalent iron ions is 4 to 18 mmol/L, the concentration of the divalent nickel ions is 150 to 500 mmol/L and the molar ratio of the divalent nickel ions to divalent iron ions is from 10/1 to 40/1.
2. The nickel-iron alloy plating solution according to claim 1 , wherein the pH is from 2.5 to 3.0.