Disclosed herein are iron-based alloys having a microstructure comprising a fine-grained ferritic matrix and having a 60+ Rockwell C surface, wherein the ferritic matrix comprises <10 μm carbide precipitates. Also disclosed are methods of welding comprising forming a crack free hardbanding weld overlay coating with such an iron-based alloy. Also disclosed are families of alloys capable of forming crack-free weld overlays after multiple welding passes.
1. An iron-based alloy having a microstructure comprising a fine-grained matrix, wherein the ferritic matrix comprises:
Nb-carbide precipitates having sizes less than 10 μm; and
hard precipitates having grain sizes less than 10 μm and comprising at least two of Mo, W, C, and B;
wherein the alloy has a Rockwell C hardness greater than 50;
and wherein the alloy comprises a combination of one or more of the following alloy chemistries, given in weight percent:
Fe 76.62 Cr 5.12 Nb 4.27 V 2.7 C 1.07 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 76.99 Cr 5.12 Nb 4.27 V 2.7 C 0.7 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 76.89 Cr 5.12 Nb 4.27 V 2.7 C 0.8 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 76.79 Cr 5.12 Nb 4.27 V 2.7 C 0.9 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 83.93 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.25 W 3 T 0.2 Si 0.52 Mn 0.5 ;
Fe 81.68 Cr 5 Nb 4.3 V 0.5 C 0.8 B 2.5 W 4 Ti 0.2 Si 0.52 Mn 0.5 ;
Fe 80.4 Cr 5 Nb 4.3 V 0.5 C 0.8 B 3 W 2 Ti 0.2 Si 0.65 Mn 1.15 ;
Fe 82.45 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.25 Mo 3 Ti 0.2 Si 2 Mn 0.5 ;
Fe 82.1 Cr 5 Nb 4 V 0.5 C 0.8 B 0.9 Mo 3.5 Ti 0.2 Si 2 Mn 1 ;
Fe 79.1 Cr 5 Nb 4 V 0.5 C 0.8 B 0.9 Mo 3.5 Ti 0.2 Si 5 Mn 1 ;
Fe 82.95 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.75 Mo 3 Ti 0.3 Si 0.4 Mn 1 ;
Fe 82.75 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.95 Mo 3 Ti 0.3 Si 0.4 Mn 1 ;
Fe 83.45 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.25 Mo 3 Ti 0.3 Si 0.4 Mn 1 ;
Fe 88 Cr 3 Nb 4.3 V 0.5 C 0.8 B 1 Mo 2 Ti 0.3 Si 0.4 Mn 1 ;
Fe 84 Cr 3 Nb 3 V 1.4 C 0.8 B 1.1 W 5 Ti 0.3 Si 0.4 Mn 1 ;
Fe 85.21 Nb 3.44 V 1.6 C 0.8 B 1.25 W 6 Ti 0.3 Si 0.4 Mn 1 ;
Fe 81.15 Nb 4 B 1 C 2 W 11.45 Si 0.15 Ti 0.25 ;
Fe 81.05 Nb 4 B 2 C 1.1 W 11.45 Si 0.15 Ti 0.25 ;
Fe 80.15 Nb 4 V 1 B 1 C 2 W 11.45 Si 0.15 Ti 0.25 ;
Fe 81.15 Nb 4 V 1 B 1 C 1 W 11.45 Si 0.15 Ti 0.25 ; and
Fe 82.05 Nb 4 B 1 C 1.1 W 11.45 Si 0.15 Ti 0.25 .
2. The iron-based alloy of claim 1 , wherein the ferritic matrix possess an average grain size less than 20 nm.
3. The iron-based alloy of claim 1 , wherein the Rockwell C hardness is greater than 55.
4. The iron-based alloy of claim 1 , wherein the alloy is capable of being deposited as a weld overlay coating.
5. The iron-based alloy of claim 1 , wherein the alloy is capable of being deposited using the MIG welding technique onto a tool joint.
6. The iron-based alloy of claim 1 , wherein the alloy capable of being deposited crack-free when deposited on a substrate that is pre-heated to at least 500° F.
7. The iron-based alloy of claim 1 , wherein the alloy is capable of being deposited crack-free on top of an existing unworn weld overlay when pre-heating a substrate of the existing unworn weld overlay to 500° F. or greater, and wherein the existing unworn weld overlay comprises a second iron-based alloy having a second microstructure comprising a second fine-grained matrix, wherein the second ferritic matrix comprises Nb-carbide precipitates having sizes less than 10 μm; and hard precipitates having grain sizes less than 10 μm and comprising at least two of Mo, W, C, and B; wherein the second alloy has a Rockwell C hardness greater than 50.
8. An iron-based alloy processing a Rockwell C hardness greater than or equal to 55, capable of being welded in two layers onto a 4137 6⅝″ O.D. toll joint to achieve a total weld thickness of at least 8/32″ without cracking; wherein the iron-based alloy comprises:
a balance of Fe;
between 4-6 wt. % Cr;
between 0.8-1.2 wt. % Mn;
between 4-5 wt. % Nb;
between 0-1 wt. % V;
between 0.6-1.1 wt. % C;
between 1.25-2.25 wt. % B;
between 2-4 wt. % Mo;
between 0.1-0.5 wt. % Ti; and
between 0.4-0.75 wt. % Si.
9. The alloy of claim 8 , wherein the alloy is capable of being deposited as a 10/32″ thick double pass weld overlay without cracking.
10. The alloy of claim 8 , wherein the alloy exhibits a mass loss less than 0.3 g lost in ASTM G65 Procedure A.
11. The alloy of claim 8 , wherein the alloy comprises a combination of one or more of the following alloy chemistries, given in weight percent:
Fe 82.95 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.75 Mo 3 Ti 0.3 Si 0.4 Mn 1 ;
Fe 82.75 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.95 Mo 3 Ti 0.3 Si 0.4 Mn 1 ;
Fe 83.45 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.25 Mo 3 Ti 0.3 Si 0.4 Mn 1 .
12. A composition of matter comprising:
a balance of Fe;
between 4-6 wt. % Cr;
between 0.8-1.2 wt. % Mn;
between 4-5 wt. % Nb;
between 0-1 wt. % V;
between 0.6-1.1 wt. % C;
between 1.25-2.25 wt. % B;
between 2-4 wt. % Mo;
between 0.1-0.5 wt. % Ti; and
between 0.4-0.75 wt. % Si.
13. The composition of matter of claim 12 , comprising a combination of one or more of the following alloy chemistries, given in weight percent:
Fe 76.621 Cr 5.12 Nb 4.27 V 2.7 C 1.07 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 76.99 Cr 5.12 Nb 4.27 V 2.7 C 0.7 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 76.89 Cr 5.12 Nb 4.27 V 2.7 C 0.8 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 76.79 Cr 5.12 Nb 4.27 V 2.7 C 0.9 B 0.82 W 7.6 Ti 0.2 Si 0.5 Mn 1.1 ;
Fe 83.93 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.5 W 3 T 0.2 Si 0.52 Mn 0.5 ;
Fe 81.68 Cr 5 Nb 4.3 V 0.5 C 0.8 B 2.5 W 4 Ti 0.2 Si 0.52 Mn 0.5 ;
Fe 80.4 Cr 5 Nb 4.3 V 0.5 C 0.8 B 3 W 2 Ti 0.2 Si 0.65 Mn 1.15 ;
Fe 82.45 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.25 Mo 3 Ti 0.2 Si 2 Mn 0.5 ;
Fe 82.1 Cr 5 Nb 4 V 0.5 C 0.8 B 0.9 Mo 3.5 Ti 0.2 Si 2 Mn 1 ;
Fe 79.1 Cr 5 Nb 4 V 0.5 C 0.8 B 0.9 Mo 3.5 Ti 0.2 Si 5 Mn 1 ;
Fe 82.95 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.75 Mo 3 Ti 0.3 Si 0.4 Mn 1 ;
Fe 82.75 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.95 Mo 3 Ti 0.3 Si 0.4 Mn 1 ; and
Fe 83.45 Cr 5 Nb 4.3 V 0.5 C 0.8 B 1.25 Mo 3 Ti 0.3 Si 0.4 Mn 1 .
14. The composition of matter of claim 12 , wherein the composition is a welding wire.
15. The composition of matter of claim 12 , wherein the composition is an alloy.
16. The composition of matter of claim 12 , wherein the composition is a weld.
17. A composition of matter comprising a combination of one or more of the following alloy chemistries, given in weight percent:
Fe 88 Cr 3 Nb 4.3 V 0.5 C 0.8 B 1.25 Mo 2 Ti 0.3 Si 0.4 Mn 1 ;
Fe 84 Cr 3 Nb 3 V 1.4 C 0.8 B 1.1 W 5 Ti 0.3 Si 0.4 Mn 1 ;
Fe 85.21 Nb 3.44 V 1.6 C 0.8 B 1.25 W 6 Ti 0.3 Si 0.4 Mn 1 ;
Fe 81.15 Nb 4 B 1 C 2 W 11.45 Si 0.15 Ti 0.25 ;
Fe 81.05 Nb 4 B 2 C 1.1 W 11.45 Si 0.15 Ti 0.25 ;
Fe 80.15 Nb 4 V 1 B 1 C 2 W 11.45 Si 0.15 Ti 0.25 ;
Fe 81.15 Nb 4 V 1 B 1 C 1 W 11.45 Si 0.15 Ti 0.25 ; and
Fe 82.05 Nb 4 B 1 C 1.1 W 11.45 Si 0.15 Ti 0.25 .
18. The composition of matter of claim 17 , wherein the composition is a welding wire.
19. The composition of matter of claim 17 , wherein the composition is an alloy.
20. The composition of matter of claim 17 , wherein the composition is a weld.