Process of leaching gold
View Patent ↗A process of leaching gold can be inexpensively and efficiently carried out from a mixture containing sulfur and gold, typically from the material containing sulfur and gold that is an intermediate product recovered by the flotation method in the hydrometallurgical method. Specifically, the mixture containing elemental sulfur and gold and an aqueous solution of hydroxide of one or more of metals of alkali metals and alkaline earth metals are combined, the hydroxides reacting with elemental sulfur to form thiosulfate of alkali and/or alkaline earth metal, and the gold thereby being leached by reaction with the thiosulfate.
1. A process of leaching gold from a copper concentrate comprising a mixture containing elemental sulfur and gold, which comprises:
preparing said mixture in which the elemental sulfur covers the surface of the gold;
contacting said mixture with an aqueous solution of one or more metal hydroxide, wherein said one or more metal is one or more metal selected from the group consisting of an alkali metal and an alkaline earth metal,
reacting said one or more metal hydroxide and elemental sulfur to produce one or more metal thiosulfate, and
leaching gold by the produced one or more metal thiosulfate;
wherein said mixture is obtained from said copper concentrate.
2. The process according to claim 1 , wherein the leaching is performed at a temperature of solution of 40° C. or more.
3. The process according to claim 1 , wherein the leaching is performed at a temperature of solution of 60° C. or more.
4. The process according to claim 1 , wherein the leaching is performed while blowing in an oxygen-containing gas.
5. The process according to claim 1 , wherein the total amount of hydroxide used is 0.5 molar equivalent or more against the elemental sulfur.
6. The process according to claim 1 , wherein the total amount of hydroxide used is 1.0-2.5 molar equivalent against the elemental sulfur.
7. The process according to claim 1 , wherein said mixture is a floats fraction recovered by a flotation method from a post-leaching residue obtained after an objective metal is leached with a hydrometallurgical method from the copper concentrate containing gold and the objective metal, wherein said floats fraction comprising a substance adhering on a surface of bubbles in said flotation method.
8. The process according to claim 1 , wherein caustic soda is used as hydroxide.