PVD ALN film with oxygen doping for a low etch rate hardmask film
The present invention generally relates to a doped aluminum nitride hardmask and a method of making a doped aluminum nitride hardmask. By adding a small amount of dopant, such as oxygen, when forming the aluminum nitride hardmask, the wet etch rate of the hardmask can be significantly reduced. Additionally, due to the presence of the dopant, the grain size of the hardmask is reduced compared to a non-doped aluminum nitride hardmask. The reduced grain size leads to smoother features in the hardmask which leads to more precise etching of the underlying layer when utilizing the hardmask.
1. A method of making a hardmask, comprising:
sputtering an aluminum target in an atmosphere containing an inert gas, a nitrogen containing gas, and an oxygen containing gas to deposit an oxygen doped polycrystalline aluminum nitride material, wherein the amount of nitrogen containing gas is more than two times the amount of oxygen containing gas; and
patterning the oxygen doped polycrystalline aluminum nitride material to form the hardmask.
2. The method of claim 1 , wherein the nitrogen containing gas comprises N 2 .
3. The method of claim 2 , wherein the oxygen containing gas comprises O 2 .
4. The method of claim 3 , wherein the ratio of inert gas to N 2 is between about 1:1 to about 1:20.
5. The method of claim 4 , wherein the ratio of inert gas to N 2 is about 1:5.
6. The method of claim 5 , wherein the ratio of N 2 to O 2 is between about 100:1 to about 20:1.
7. The method of claim 6 , wherein the ratio of N 2 to O 2 is about 50:3.
8. The method of claim 1 , wherein sputtering occurs at a temperature between about 25 degrees Celsius and about 500 degrees Celsius.
9. The method of claim 8 , wherein the sputtering occurs at a chamber pressure of between about 1 mTorr and about 100 mTorr.
10. The method of claim 1 , wherein the sputtering is DC sputtering or pulsed DC sputtering.
11. A method of making a hardmask, comprising:
sputtering an aluminum nitride target in an atmosphere containing an inert gas, a nitrogen containing gas, and an oxygen containing gas to form an oxygen doped polycrystalline aluminum nitride material, wherein the amount of nitrogen containing gas is more than two times the amount of oxygen containing gas; and
patterning the oxygen doped polycrystalline aluminum nitride material to form the hardmask.
12. The method of claim 11 , wherein the sputtering is RF sputtering.