Polyurea capsules prepared with a polyisocyanate and cross-linking agent
Polyurea capsules that encapsulate active materials in polymeric walls resulting from the polymerization of an aromatic or aliphatic polyisocyanate and a cross-linking agent are provided as are consumer products containing said polyurea capsules and for methods for producing such capsules.
1. A method for preparing a polyurea capsule composition comprising:
(a) preparing an oil phase comprising an active material and a polyisocyanate;
(b) preparing a surfactant solution;
(c) emulsifying the oil phase into the surfactant solution to form a fragrance emulsion;
(d) adding a cross-linking agent to the fragrance emulsion to form a capsule slurry;
(e) curing the capsule slurry;
(f) adding a salt to the cured capsule slurry; and
(g) washing the capsule slurry with water,
wherein the active material is a fragrance oil present at a level of about 5% to about 80% of the capsule composition; the polyisocyanate, added at a level of about 0.1% to about 10% by weight of the capsule composition, consists of a trimethylol propane-adduct of xylylene diisocyanate; the surfactant is added at a level of about 0.1% to about 5% by weight of the capsule composition; the cross-linking agent, added at a level of about 0.1% to about 5% by weight of capsule composition, is N,N′-bis(3-aminopropyl)-1,3-propanediamine, chitosan, nisin, or a combination thereof; an encapsulating polymer is formed by the polymerization reaction between the polyisocyanate and the cross-linking agent; and the encapsulating polymer encapsulates the active material.