Low alpha particle emission electrically-conductive coating
View Patent ↗An electrically conductive paste providing low alpha particle emission is provided. A resin and conductive particles are mixed, and a curing agent is added. A solvent is subsequently added. The electrically conductive paste including a resin compound is formed by mixing the mixture in a high shear mixer. The electrically conductive paste can be applied to a surface of an article to form a coating, or can be molded into an article. The solvent is evaporated, and the electrically conductive paste is cured to provide a graphite-containing resin compound. The graphite-containing resin compound is electrically conductive, and provides low alpha particle emission at a level suitable for a low alpha particle emissivity coating.
1. An article of manufacture comprising:
an electrode;
a sample tray in an alpha particle counter, wherein a bottommost surface of said sample tray is in direct physical contact with a topmost surface of said electrode; and
an electrically conductive material, wherein said electrically conductive material is present directly on a topmost surface of said sample tray, and wherein said electrically conductive material comprises a cross-linked polymer of a resin in which conductive particles are embedded therein and having an alpha particle emissivity less than 2 α particles/khr-cm 2 .
2. The article of manufacture of claim 1 , wherein a predominant portion of said conductive particles has a maximum lateral dimension in a range from less than 1 micrometer to 100 micrometers.
3. The article of manufacture of claim 1 , wherein a volume percentage of conductive particles with respect to a total volume of said resin and said conductive particles is in a range from 0.1% to 40%.
4. The article of manufacture of claim 1 , wherein a purity of conductive particles in said conductive particles is greater than 99% in atomic percentage.
5. The article of manufacture of claim 1 , wherein said resin has a viscosity in a range from 10 −2 Pa-s to 10 3 Pa-s.
6. The article of manufacture of claim 1 , wherein said electrically conductive material comprises graphite.
7. The article of manufacture of claim 1 , wherein said electrically conductive material comprises carbon nanotubes.
8. The article of manufacture of claim 1 , wherein said electrically conductive material is particles of an elemental metal selected from Al, Ti, Fe, Ni, Cu, Mo, Sn, Ta, W, Pt, and Au; particles of intermettalic alloys of at least two of Al, Ti, Fe, Ni, Cu, Mo, Sn, Ta, W, Pt, and Au; or a conductive metal compound including at least one of Al, Ti, Fe, Ni, Cu, Mo, Sn, Ta, W, Pt, and Au.