Semiconductor device connected by anisotropic conductive film

1. A liquid crystal display device, comprising:

a first connecting member having a first electrode;

a second connecting member having a second electrode; and

an anisotropic conductive film filling an entire space between the first connecting member and the second connecting member, the anisotropic conductive film electrically connecting the first and second electrodes to each other, and the anisotropic conductive film including:

a polymer binder resin selected from the group consisting of a polyimide resin, a polyamide resin, a phenoxy resin, a polyvinyl butyral resin, and in combination thereof;

an epoxy resin;

conductive particles;

a curing agent; and

silica nanoparticles,

wherein the epoxy resin includes a naphthalene ring-containing epoxy resin and a dicyclopentadiene ring-containing epoxy resin,

the naphthalene ring-containing epoxy resin is present in an amount of 300 parts by weight to 500 parts by weight, based on 100 parts by weight of the dicyclopentadiene ring-containing epoxy resin, and

the anisotropic conductive film has a melting viscosity from 0.2 Pa·s to 0.5 Pa·s at 150° C.,

wherein the anisotropic conductive film includes:

5 wt% to 35 wt% of the polymer binder resin;

5 wt% to 25 wt% of the epoxy resin;

5 wt% to 30 wt% of the conductive particles;

30 wt% to 50 wt% of the curing agent, and

0.1 wt% to 20 wt% of the silica nanoparticles, based on a total amount of the anisotropic conductive film in terms of solid content, and

wherein, after curing and after being subjected to conditions of 85° C. and 85% RH for 500hours, the anisotropic conductive film has a bubble area between the first and second electrodes of 20% or less in a space area therebetween.

2. The liquid crystal display device as claimed in claim 1 , wherein the anisotropic conductive film has a moisture absorption rate of 0.8% or less.

3. The liquid crystal display device as claimed in claim 1 , wherein the anisotropic conductive film has an adhesive strength from 30 N/25 mm to 100 N/25 mm.

4. The liquid crystal display device as claimed in claim 1 , wherein the dicyclopentadiene ring-containing epoxy resin has a melting viscosity from 0.1 Pa·s to 1 Pa·s at 150° C.

5. The liquid crystal display device as claimed claim 1 , wherein the anisotropic conductive film, after curing and after being subjected to conditions of 85° C. and 85% RH for 500 hours, has a connection resistance of 10Ω or less.

6. The liquid crystal display device as claimed in claim 5 , wherein the curing is performed at 190° C. to 210° C. for 5 seconds to 10 seconds at a load of 50 MPa to 80 MPa.