Two-step batch process for coating surgical needles

1. A method of batch coating a plurality of surgical needles, comprising:

providing a plurality of surgical needles, wherein at least some of the needles are in contact with each other;

then, immersing the needles in a bath containing a silicone coating solution, said solution comprising a cross-linkable siloxane polymer, a non-cross-linkable siloxane polymer, a cross-linking agent, a platinum catalyst, and a solvent to provide a coating on each needle;

next, removing the needles from the bath;

then, partially curing the coatings on the needles at a partial cure temperature for a first time period such that the coatings are partially cured, wherein the partial cure temperature is about 90° C. to about 100° C.;

then, mechanically separating the needles; and

finally, fully curing the coatings on the needles at a full cure temperature for a second time period such that the coatings are fully cured, the full cure temperature being higher than the partial cure temperature, wherein damage to the coatings after mechanically separating the needles is substantially repaired or mitigated by a limited re-flow of the partially cured coatings during the second time period.

2. The method of claim 1 , wherein the needles are placed in a porous containment vessel prior to immersing the needles in the coating bath, and the needles and the vessel are both immersed in the coating bath.

3. The method of claim 1 , wherein the silicone coating comprises vinyl terminated polydimethyldisiloxane; methyl terminated polydimethyldisiloxane;

polymethylhydro siloxane; and a platinum catalyst comprising platinum divinyltetramethyldisiloxane ethynylcyclohexanol complex.

4. The method of claim 1 , comprising the additional step of removing substantially all of the solvent from the coating prior to the partial curing step.

5. The method of claim 1 , wherein the second temperature is at least about 120° C.

6. The method of claim 1 , wherein the time for the partial cure is at least about one hour and the time for the second full cure is at least one hour.

7. The method of claim 1 , further comprising the step of placing the needles on a dying tray after removing the needles from the coating bath.

8. The method of claim 1 , wherein the first and second curing steps are done in an oven.

9. The method of claim 1 , wherein the cross-linkable siloxane is selected from the group consisting of dimethylvinylsilyl-terminated polydimethyl siloxane, polydiphenylsilane-dimethylsiloxane copolymer, polyphenylmethylsiloxane, polyfluoropropylmethyl-dimethylsiloxane copolymer and polydiethylsiloxane.

10. The method of claim 1 , wherein the non-cross-linkable siloxane is selected from the group consisting of trimethylsilyl-terminated polydimethyl siloxane, polyalkylmethylsiloxane, polydiethylsiloxane, polyfluoropropylmethylsiloxane, polyoctylmethylsiloxane, polytetradecylmethylsiloxane, polyoctadecylmethylsiloxane, polyalkylmethyl dimethylsiloxane, and polyhexadecymethylsiloxane-dimethyl siloxane.

11. The method of claim 1 , wherein the cross-linking agent is selected from the group consisting of polymethylhydrosiloxane, polymethylhydro-co-polydimethylsiloxane, polyethyhydrosiloxane, polymethylhydrosiloxane-co-octylmethylsiloxane, and polymethylhydrosiloxane-co-methylphenylsiloxane.

12. The method of claim 1 , wherein the catalyst is the Ashby-Karstedt catalyst.

13. The method of claim 1 , wherein the catalyst comprises a platinum complex catalyst (platinum vinyltetramethyldisiloxane ethynylcyclohexanol complex) having the formula:

Pt[(CH 2 ═CH)(Me) 2 Si] 2 O⋅C 6 H 10 (OH)(C≡CH).