Dried hydrogel, dried vitrigel membrane, and methods for producing the same

1. A method for producing a dried vitrigel membrane having a desired shape, comprising the following steps of:

placing a wall surface mold, which is a cylindrical frame body not having a top surface and a bottom surface and having a shape the same as the desired shape, onto a substrate such that a gap is formed between a surface of the substrate and an underside of the cylindrical frame of the wall surface mold;

adding a hydrosol to the inside of the wall surface mold;

forming a hydrogel by gelation of the hydrosol in the inside of the wall surface mold;

allowing a part of a free water within the hydrogel to discharge horizontally through the gap between the surface of the substrate and the underside of the cylindrical frame of the wall surface mold while maintaining the hydrogel in the inside of the wall surface mold;

removing the wall surface mold from the top of the substrate;

drying the hydrogel to remove residual free water, thereby fabricating a vitrified dried hydrogel;

rehydrating the dried hydrogel to fabricate a vitrigel membrane; and

redrying the vitrigel membrane to remove free water, thereby fabricating a vitrified dried vitrigel membrane, which does not have an amorphous outer peripheral edge.

2. The method for producing a dried vitrigel membrane according to claim 1 , wherein in the adding step, a support is introduced into the hydrosol in the inside of the wall surface mold.

3. The method for producing a dried vitrigel membrane according to claim 1 , wherein in the allowing step, an amount of the free water within the hydrogel is reduced to from about ¼ to ¾.

4. The method for producing a dried vitrigel membrane according to claim 1 , wherein in the redrying step, the dried vitrigel membrane is vitrified on a film possessing a capacity facilitating the detachability of the dried vitrigel membrane.

5. The method for producing a dried vitrigel membrane according to claim 4 , wherein the film is Parafilm.