Cathode active material for lithium ion battery, cathode for lithium ion battery, and lithium ion battery
View Patent ↗There is provided a cathode active material for a lithium ion battery having good battery properties. The cathode active material for a lithium ion battery is represented by a composition formula: Li(Li x Ni 1-x-y M y )O 2+α wherein M is one or more selected from Sc, Ti, V, Cr, Mn, Fe, Co, Cu, Zn, Ga, Ge, Al, Bi, Sn, Mg, Ca, B, and Zr; 0≦x≦0.1; 0<y≦0.7; and α>0, and has a moisture content measured by Karl Fischer titration at 300° C. of 1100 ppm or lower.
1. A cathode active material for a lithium ion battery, represented by a composition formula:
Li(Li x Ni 1-x-y M y )O 2+α
wherein M is one or more selected from Sc, Ti, V, Cr, Mn, Fe, Co, Cu, Zn, Ga, Ge, Al, Bi, Sn, Mg, Ca, B, and Zr; 0≦x≦0.1; 0<y<0.7; and α>0,
wherein a first moisture content measured by Karl Fischer titration at 300° C. is 1100 ppm or lower and,
a difference between the first moisture content measured by Karl Fischer titration at 300° C. and a second moisture content measured by Karl Fischer titration at 150° C. is 100 to 500 ppm;
further wherein a third moisture content measured by Karl Fischer titration at 150° C. is 300 ppm or lower after the cathode active material is left at a dew point of −80° C. for 24 hours.
2. The cathode active material for a lithium ion battery according to claim 1 , wherein the first moisture content measured by Karl Fischer titration at 300° C. is 800 ppm or lower.
3. The cathode active material for a lithium ion battery according to claim 1 , wherein the M is one or more selected from Mn and Co.
4. The cathode active material for a lithium ion battery according to claim 1 , wherein α>0.1 in the composition formula.
5. The cathode active material for a lithium ion battery according to claim 4 , wherein α>0.1 in the composition formula.
6. The cathode active material for a lithium ion battery according to claim 1 , wherein the second moisture content measured by Karl Fischer titration at 150° C. is 300 ppm or lower.
7. The cathode active material for a lithium ion battery according to claim 6 , wherein the second moisture content measured by Karl Fischer titration at 150° C. is 200 ppm or lower.
8. The cathode active material for a lithium ion battery according to claim 1 , wherein the difference between the first moisture content measured by Karl Fischer titration at 300° C. and the second moisture content measured by Karl Fischer titration at 150° C. is 100 to 130 ppm.
9. The cathode active material for a lithium ion battery according to claim 1 , wherein a fourth moisture content measured by Karl Fischer titration at 150° C. is 1500 ppm or lower after the cathode active material is exposed to air at a humidity of 50% and at 25° C. for 24 hours.
10. The cathode active material for a lithium ion battery according to claim 9 , wherein a fourth moisture content measured by Karl Fischer titration at 150° C. is 1200 ppm or lower after the cathode active material is exposed to air at a humidity of 50% and at 25° C. for 24 hours.
11. The cathode active material for a lithium ion battery according to claim 1 , wherein the third moisture content measured by Karl Fischer titration at 150° C. is 200 ppm or lower after the cathode active material is left at a dew point of −80° C. for 24 hours.
12. A cathode for a lithium ion battery, using a cathode active material for a lithium ion battery according to claim 1 .
13. A lithium ion battery, using a cathode for a lithium ion battery according to claim 12 .