Polyoxometalate and heteropolyoxometalate compositions and methods for their use
View Patent ↗The present invention relates to novel compositions comprising a metal component selected from a group chosen from at least one polyoxometalate, at least one heteropolyoxometalate and a mixture thereof; and, at least one organic component. The present invention also relates to methods of preparing the nanorod arrays and the nanorod materials and films. The present invention also relates to novel compositions to generate metal-oxide rich films, and also relates to processes for via or trench filling, reverse via or trench filling and imaging with underlayers. The materials are useful in wide range of manufacturing applications in many industries, including the semiconductor devices, electro-optical devices and energy storage industry.
1. A method for generating nanorod arrays comprising the steps of:
a) coating a composition onto a substrate to form a film;
b) a first heating step comprising heating the film in a range from 200° C. to 350° C.; and,
c) a second heating step comprising heating the film in a range from 500° C. to 900° C.,
wherein the composition comprises:
a) a metal component selected from a group chosen from at least one polyoxometalate, at least one heteropolyoxometalate and a mixture thereof;
b) at least one organic component comprising one or more functional groups chosen from an alcohol, a phenol, an amine, an amide, an imide, a carboxylic acid, a ketone, a ester, a lactone, a lactam, a 2-hydroxy aniline, and a β-dicarbonyl having at least one hydrogen on the connecting carbon; and,
c) at least one solvent.
2. The method of claim 1 , wherein the second heating is performed at a ramping rate of 40° C. to 100° C. per minute either in a single or a multiple step process.
3. The method of claim 1 further comprising the step of removing the film from the substrate after the first heating step and prior to the second heating step and wherein the second heating step is of the removed film.
4. A method of coating a composition onto a substrate comprising an electrospinning, wherein the composition is first introduced into an electrospinning chamber and wherein the composition comprises:
a) a metal component selected from a group chosen from at least one polyoxometalate, at least one heteropolyoxometalate and a mixture thereof;
b) at least one organic component comprising one or more functional groups chosen from an alcohol, a phenol, an amine, an amide, an imide, a carboxylic acid, a ketone, a ester, a lactone, a lactam, a 2-hydroxy aniline, and a β-dicarbonyl having at least one hydrogen on the connecting carbon; and,
c) at least one solvent.
5. The method according to claim 4 , where the electrospinning is gas assisted.