Etching of plastic using acidic solutions containing trivalent manganese
View Patent ↗A method of preparing a solution capable of etching a platable plastic. The method comprises the steps of: (a) providing an electrolyte comprising a solution of manganese(II) in a solution of 9 to 15 molar sulfuric acid or phosphoric acid to an electrolytic cell; (b) applying a current to the electrolytic cell, wherein the electrolytic cell comprises an anode and a cathode; and (c) oxidizing the electrolyte to form manganese(III) ions, wherein the manganese(III) ions form a metastable sulfate complex. Thereafter, a platable plastic may be immersed in the metastable sulfate complex for a period of time to etch the platable substrate prior to subsequent plating steps.
1. A method comprising:
a. providing a substrate comprising one or more organic polymers;
b. providing a composition comprising dissolved Mn(II) ions, dissolved Mn(III) ions, and one or more acids; and
c. contacting the substrate comprising the one or more organic polymers with the composition to etch a surface of the substrate.
2. The method according to claim 1 , wherein the concentration of Mn(II) ions in the composition is in the range of between about 0.005 molar and saturation.
3. The method according to claim 1 , wherein a portion of the Mn(II) ions are oxidized to Mn(III) ions by electrolysis.
4. The method according to claim 1 , wherein the temperature of the composition is in the range of between about 30° C. and about 80° C.
5. The method according to claim 1 , wherein the substrate is contacted with the composition for about 20 to about 30 minutes.
6. The method according to claim 2 , wherein the composition is agitated.
7. The method according to claim 1 , wherein the one or more acids comprise sulfuric acid or phosphoric acid.
8. The method according to claim 7 , wherein the one or more acids comprise sulfuric acid.
9. The method according to claim 8 , wherein the concentration of the sulfuric acid is in the range of between about 9 and about 15 molar.
10. The method according to claim 9 , wherein the concentration of the sulfuric acid is in the range of between about 12 and about 13 molar.
11. The method according to claim 9 , wherein the composition further comprises colloidal manganese dioxide.