Fibrous sheet that disintegrates in water, process for manufacturing said fibrous sheet, core consisting of strips of said fibrous sheet
A fibrous sheet having a basis weight of between 20 and 1000 g/m 2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm 2 , is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.
1. A process for manufacturing a fibrous sheet comprising at least 30% of papermaking fibres, that disintegrates in less than 120 seconds in water, comprising:
suspending fibres in water;
forming at least a first fibrous ply and a second fibrous ply with said fibres:
depositing a starch on the second fibrous ply;
depositing the first fibrous ply on the second fibrous ply;
joining the two plies together as a fibrous sheet and drying the fibrous sheet, wherein the starch is deposited in a dry state on the second ply.
2. The process according to claim 1 , wherein the starch is water-soluble.
3. The process according to claim 1 , wherein the starch is water insoluble.
4. The process according to claim 1 , wherein the deposited starch is a combination of a water-soluble and water-insoluble starch.
5. The process according to claim 1 , wherein the starch is deposited in powder form.
6. The process according to claim 1 , wherein at least a third fibrous ply is formed and deposited on said two plies with interposition or not of starch.