Method of manufacturing semiconductor device
In a manufacturing process of a transistor including an oxide semiconductor film, oxygen doping treatment is performed on the oxide semiconductor film, and then heat treatment is performed on the oxide semiconductor film and an aluminum oxide film provided over the oxide semiconductor film. Consequently, an oxide semiconductor film which includes a region containing more oxygen than a stoichiometric composition is formed. The transistor formed using the oxide semiconductor film can have high reliability because the amount of change in the threshold voltage of the transistor by a bias-temperature stress test (BT test) is reduced.
1. A method for manufacturing a semiconductor device, the method comprising the steps of:
forming a first insulating film;
forming a semiconductor film comprising indium, gallium, zinc, and oxygen over the first insulating film;
performing a first heat treatment on the semiconductor film;
forming a source electrode and a drain electrode over the semiconductor film after performing the first heat treatment;
forming a second insulating film over the semiconductor film, the source electrode, and the drain electrode;
adding oxygen into the semiconductor film after forming the second insulating film; and
performing a second heat treatment on the semiconductor film and the second insulating film after adding oxygen.
2. The method according to claim 1 , wherein the second insulating film is an aluminum oxide film.
3. The method according to claim 1 , wherein the first heat treatment is performed in a first atmosphere comprising an inert gas and then performed in a second atmosphere comprising oxygen.
4. The method according to claim 1 , wherein the first insulating film and the semiconductor film are successively formed without exposure to air.
5. The method according to claim 1 , wherein the first heat treatment is performed at a temperature higher than or equal to 250° C. and lower than or equal to 700° C.
6. The method according to claim 1 , wherein the second heat treatment is performed at a temperature higher than or equal to 350° C. and lower than or equal to 650° C.
7. The method according to claim 1 , wherein oxygen is added into the semiconductor film by an oxygen doping treatment.
8. The method according to claim 7 , wherein the oxygen doping treatment is an oxygen ion implantation treatment or an oxygen plasma doping.
9. The method according to claim 1 , wherein the semiconductor film comprises a crystalline region.
10. The method according to claim 1 , wherein the semiconductor film has an island shape.
11. A method for manufacturing a semiconductor device, the method comprising the steps of:
forming a gate electrode;
forming a first insulating film over the gate electrode;
forming a semiconductor film comprising indium, gallium, zinc, and oxygen over the first insulating film;
performing a first heat treatment on the semiconductor film;
forming a source electrode and a drain electrode over the semiconductor film after performing the first heat treatment;
forming a second insulating film over the semiconductor film, the source electrode, and the drain electrode;
adding oxygen into the semiconductor film after forming the second insulating film; and
performing a second heat treatment on the semiconductor film and the second insulating film after adding oxygen.
12. The method according to claim 11 , wherein the second insulating film is an aluminum oxide film.
13. The method according to claim 11 , wherein the first heat treatment is performed in a first atmosphere comprising an inert gas and then performed in a second atmosphere comprising oxygen.
14. The method according to claim 11 , wherein the first insulating film and the semiconductor film are successively formed without exposure to air.
15. The method according to claim 11 , wherein the first heat treatment is performed at a temperature higher than or equal to 250° C. and lower than or equal to 700° C.
16. The method according to claim 11 , wherein the second heat treatment is performed at a temperature higher than or equal to 350° C. and lower than or equal to 650° C.
17. The method according to claim 11 , wherein oxygen is added into the semiconductor film by an oxygen doping treatment.
18. The method according to claim 17 , wherein the oxygen doping treatment is an oxygen ion implantation treatment or an oxygen plasma doping.
19. The method according to claim 11 , wherein the semiconductor film comprises a crystalline region.
20. The method according to claim 11 , wherein the semiconductor film has an island shape.
21. A method for manufacturing a semiconductor device, the method comprising the steps of:
forming a first insulating film;
forming a semiconductor film comprising indium, gallium, zinc, and oxygen over the first insulating film;
performing a first heat treatment on the semiconductor film;
forming a source electrode and a drain electrode over the semiconductor film after performing the first heat treatment;
forming a second insulating film over the semiconductor film, the source electrode, and the drain electrode;
adding oxygen into the semiconductor film after forming the second insulating film;
forming a gate electrode over the second insulating film;
forming a third insulating film over the gate electrode; and
performing a second heat treatment on the semiconductor film and the third insulating film after adding oxygen.
22. The method according to claim 21 , wherein the third insulating film is an aluminum oxide film.
23. The method according to claim 21 , wherein the first heat treatment is performed in a first atmosphere comprising an inert gas and then performed in a second atmosphere comprising oxygen.
24. The method according to claim 21 , wherein the first insulating film and the semiconductor film are successively formed without exposure to air.
25. The method according to claim 21 , wherein the first heat treatment is performed at a temperature higher than or equal to 250° C. and lower than or equal to 700° C.
26. The method according to claim 21 , wherein the second heat treatment is performed at a temperature higher than or equal to 350° C. and lower than or equal to 650° C.
27. The method according to claim 21 , wherein oxygen is added into the semiconductor film by an oxygen doping treatment.
28. The method according to claim 27 , wherein the oxygen doping treatment is an oxygen ion implantation treatment or an oxygen plasma doping.
29. The method according to claim 21 , wherein the semiconductor film comprises a crystalline region.
30. The method according to claim 21 , wherein the semiconductor film has an island shape.
31. A method for manufacturing a semiconductor device, the method comprising the steps of:
forming a first insulating film;
forming a semiconductor film comprising indium, zinc, and oxygen over the first insulating film;
performing a first heat treatment on the semiconductor film;
forming a source electrode and a drain electrode over the semiconductor film after performing the first heat treatment;
forming a second insulating film over the semiconductor film, the source electrode, and the drain electrode;
performing an oxygen doping treatment after forming the second insulating film; and
performing a second heat treatment on the semiconductor film and the second insulating film after performing the oxygen doping treatment.
32. The method according to claim 31 , wherein the semiconductor film comprises gallium.
33. The method according to claim 31 , wherein the second insulating film is an aluminum oxide film.
34. The method according to claim 31 , wherein the first heat treatment is performed in a first atmosphere comprising an inert gas and then performed in a second atmosphere comprising oxygen.
35. The method according to claim 31 , wherein the first insulating film and the semiconductor film are successively formed without exposure to air.
36. The method according to claim 31 , wherein the first heat treatment is performed at a temperature higher than or equal to 250° C. and lower than or equal to 700° C.
37. The method according to claim 31 , wherein the second heat treatment is performed at a temperature higher than or equal to 350° C. and lower than or equal to 650° C.
38. The method according to claim 31 , wherein the semiconductor film comprises a crystalline region.
39. The method according to claim 31 , wherein the semiconductor film has an island shape.
40. The method according to claim 31 , wherein the oxygen doping treatment is an oxygen ion implantation treatment or an oxygen plasma doping.
41. A method for manufacturing a semiconductor device, the method comprising the steps of:
forming a gate electrode;
forming a first insulating film over the gate electrode;
forming a semiconductor film comprising indium, zinc, and oxygen over the first insulating film;
performing a first heat treatment on the semiconductor film;
forming a source electrode and a drain electrode over the semiconductor film after performing the first heat treatment;
forming a second insulating film over the semiconductor film, the source electrode, and the drain electrode;
performing an oxygen doping treatment after forming the second insulating film; and
performing a second heat treatment on the semiconductor film and the second insulating film after performing the oxygen doping treatment.
42. The method according to claim 41 , wherein the semiconductor film comprises gallium.
43. The method according to claim 41 , wherein the second insulating film is an aluminum oxide film.
44. The method according to claim 41 , wherein the first heat treatment is performed in a first atmosphere comprising an inert gas and then performed in a second atmosphere comprising oxygen.
45. The method according to claim 41 , wherein the first insulating film and the semiconductor film are successively formed without exposure to air.
46. The method according to claim 41 , wherein the first heat treatment is performed at a temperature higher than or equal to 250° C. and lower than or equal to 700° C.
47. The method according to claim 41 , wherein the second heat treatment is performed at a temperature higher than or equal to 350° C. and lower than or equal to 650° C.
48. The method according to claim 41 , wherein the semiconductor film comprises a crystalline region.
49. The method according to claim 41 , wherein the semiconductor film has an island shape.
50. The method according to claim 41 , wherein the oxygen doping treatment is an oxygen ion implantation treatment or an oxygen plasma doping.
51. A method for manufacturing a semiconductor device, the method comprising the steps of:
forming a first insulating film;
forming a semiconductor film comprising indium, zinc, and oxygen over the first insulating film;
performing a first heat treatment on the semiconductor film;
forming a source electrode and a drain electrode over the semiconductor film after performing the first heat treatment;
forming a second insulating film over the semiconductor film, the source electrode, and the drain electrode;
performing an oxygen doping treatment after forming the second insulating film;
forming a gate electrode over the second insulating film;
forming a third insulating film over the gate electrode; and
performing a second heat treatment on the semiconductor film and the third insulating film after performing the oxygen doping treatment.
52. The method according to claim 51 , wherein the semiconductor film comprises gallium.
53. The method according to claim 51 , wherein the third insulating film is an aluminum oxide film.
54. The method according to claim 51 , wherein the first heat treatment is performed in a first atmosphere comprising an inert gas and then performed in a second atmosphere comprising oxygen.
55. The method according to claim 51 , wherein the first insulating film and the semiconductor film are successively formed without exposure to air.
56. The method according to claim 51 , wherein the first heat treatment is performed at a temperature higher than or equal to 250° C. and lower than or equal to 700° C.
57. The method according to claim 51 , wherein the second heat treatment is performed at a temperature higher than or equal to 350° C. and lower than or equal to 650° C.
58. The method according to claim 51 , wherein the semiconductor film comprises a crystalline region.
59. The method according to claim 51 , wherein the semiconductor film has an island shape.
60. The method according to claim 51 , wherein the oxygen doping treatment is an oxygen ion implantation treatment or an oxygen plasma doping.