Cold field electron emitters based on silicon carbide structures
A cold cathode field emission electron source capable of emission at levels comparable to thermal sources is described. Emission in excess of 6 A/cm 2 at 7.5 V/μm is demonstrated in a macroscopic emitter array. The emitter has a monolithic and rigid porous semiconductor nanostructure with uniformly distributed emission sites, and is fabricated through a room temperature process which allows for control of emission properties. These electron sources can be used in a wide range of applications, including microwave electronics and x-ray imaging for medicine and security.
1. A method of forming a monolithic, homogeneous, and porous silicon carbide field emitter having a plurality of discrete emission projections extending from a face of the field emitter, the method comprising:
providing a silicon carbide substrate;
providing an anodizing solution including (i) at least one reducing agent, (ii) at least one oxidizer, and (iii) water;
electrochemically etching either face of the silicon carbide substrate with the anodizing solution for an effective period of time to thereby form a porous silicon carbide substrate;
subjecting the face of the porous silicon carbide substrate to ion etching to thereby form a silicon carbide field emitter having a plurality of discrete emission projections of porous silicon carbide extending from the face of the field emitter.
2. The method of claim 1 wherein the electrochemically etching uses a voltage within a range of from about 10V to about 100V.
3. The method of claim 2 wherein the electrochemically etching uses a voltage of about 20V.
4. The method of claim 1 wherein the period of time is at least 1 minute.
5. The method of claim 4 wherein the period of time is from about 5 minutes to about 4 hours.
6. The method of claim 1 wherein the reducing agent of the anodizing solution is hydrofluoric acid and the oxidizer of the anodizing solution is ethanol.
7. The method of claim 1 wherein the anodizing solution includes from about 1% to about 30% hydrofluoric acid and from about 5% to about 30% ethanol.
8. The method of claim 1 wherein ion etching is performed by focused ion beam (FIB) etching which may be gas-assisted, or reactive ion etching (RIE).
9. The method of claim 1 wherein the discrete emission projections have an average height within a range of from about 1 micron to about 100 microns, an average thickness of from about 0.1 microns to about 10 microns, and an average spacing of from about 1 micron to about 100 microns.
10. The method of claim 1 wherein the silicon carbide field emitter has an average pore wall thickness of from about 10 nm to about 1,000 nm, and an average pore size of from about 10 nm to about 1,000 nm.
11. The method of claim 1 wherein the electrochemically etching is performed at ambient temperature.