Guidewire with varying properties
A method of making a core metal element for a medical guidewire including providing a wire of nickel titanium alloy having a length that includes a proximal portion having a first diameter and a distal portion having a second diameter. The method further includes applying cold work to the distal portion and not applying cold work to the proximal portion, thereby imparting to the distal portion a third diameter that is smaller than the second diameter; and then applying a reducing process to the wire whereby the proximal portion is reduced to have a fourth diameter that is less than the first diameter.
1. A method of making a medical guidewire core element comprising:
providing a wire of nickel titanium alloy with superelastic properties having a proximal end and a distal end, wherein a first length separates the proximal end from the distal end;
applying cold work to the wire through a rotary swaging machine in a sequence that comprises:
swaging the wire over a second length that includes the distal end by using a die set having a first diameter wherein the second length is less than the first length;
swaging the wire over a third length that includes the distal end by using a die set having a second diameter, the third length being less than the second length, and the second diameter being less than the first diameter; and
applying a reducing process to the wire, following swaging the wire over the second length and the third length, whereby the wire is reduced to have a constant diameter over the first length wherein the reducing process includes applying centerless grinding.
2. The method of claim 1 , wherein wherein the second length is between 16 mm and 20 mm and the third length is between 10 mm and 14 mm.
3. The method of claim 1 , wherein wherein the first diameter is between 0.356 mm and 0.436 mm and the second diameter is between 0.347 mm and 0.425 mm.
4. The method of claim 1 , further including swaging the wire over a fourth length of the wire that includes the distal end by using a die set having a third diameter, wherein the fourth length is less than the third length and the third diameter is less than the second diameter.
5. A method of making a medical guidewire core element comprising:
providing a wire of nickel titanium alloy with superelastic properties having a proximal end and a distal end, wherein a first length separates the proximal end from the distal end;
applying cold work to the wire through a rotary swaging machine in a sequence that comprises:
swaging the wire over a second length between a first distal point and a first proximal point by using a die set having a first diameter;
swaging the wire over a third length between a second distal point and a second proximal point by using a die set having a second diameter, the second diameter being larger than the first diameter, further including selecting the second distal point to coincide with the first proximal point; and
applying a reducing process to the wire, following swaging the wire over the second length and the third length, whereby the wire is reduced to having a constant diameter over the first length wherein the reducing process includes applying centerless grinding.
6. The method of claim 5 , wherein wherein the second length is between 4 mm and 8 mm and the third length is between 4 mm and 8 mm.
7. The method of claim 5 , wherein the first diameter is between 0.338 mm and 0.414 mm and the second diameter is between 0.347 mm and 0.425 mm.
8. The method of claim 5 , further including selecting the first distal point to coincide with the distal end.
9. The method of claim 5 , further including swaging the wire over a fourth length of the wire between a third distal point and a third proximal point by using a die set having a third diameter, the third diameter being larger than the second diameter, and further including selecting the third distal point to coincide with the second proximal point.