Ion exchange processes and chemically strengthened glass substrates resulting therefrom
A method of performing ion exchange of a thin, flexible glass substrate having an average thickness equal to or less than about 0.3 mm to chemically strengthen the glass substrate is disclosed. The chemically strengthened glass substrate comprises a first compressive stress layer having a first depth of layer, and a second compressive stress layer having a second depth of layer, the first and second stress layers being separated by a layer of tensile stress. A laminated article comprising the chemically strengthened glass substrate is also described.
1. A laminate article comprising:
a first substrate; and
a second substrate comprising a first surface and a second surface opposite the first surface, wherein an average thickness of the second substrate between the first surface and the second surface is equal to or less than about 0.3 mm, the second surface being bonded to the first substrate, the second substrate comprising:
a glass substrate including;
a first compressive stress layer extending inward toward a center of the glass substrate from the first surface comprising a first depth of layer DOL 1 ;
a second compressive stress layer extending inward toward the center of the glass substrate from the second surface comprising a second depth of layer DOL 2 ;
wherein DOL 1 is greater than DOL 2 ; and
wherein DOL 1 is greater than 25% of the average thickness of the glass substrate.
2. The laminate article according to claim 1 , wherein the first substrate comprises a polymer.
3. The laminate article according to claim 1 , wherein the first substrate comprises metal.
4. The laminate article of claim 1 , wherein DOL 1 is at least 2% greater than DOL 2 .
5. The laminate article of claim 1 , wherein DOL 1 is at least 6% greater than DOL 2 .
6. The laminate article of claim 1 , wherein DOL 1 is at least 10% greater than DOL 2 .
7. The laminate article of claim 1 , wherein the compressive stress at the first surface of the second substrate is at least 500 MPa.
8. The laminate article of claim 1 , wherein the compressive stress at the first surface of the second substrate is at least 950 MPa.
9. The laminate article of claim 1 , wherein the compressive stress at the second surface of the second substrate is at least 850 MPa.