Coated container
View Patent ↗The present invention relates generally to the field of polyolefin containers. One aspect of the invention is a polyolefin container coated with a gas barrier coating. In particular, the present invention relates to a polyolefin container coated with a gas barrier coating comprising a first layer of hydrogenated amorphous silicon nitride and a second layer of hydrogenated amorphous carbon. The hydrogenated amorphous silicon nitride layer may be deposited on the container, and the hydrogenated amorphous carbon layer may be deposited on the hydrogenated amorphous silicon nitride layer. A further aspect of the invention is a process for coating a polyolefin container comprising the steps of depositing a layer of hydrogenated amorphous silicon nitride on a polyolefin container by plasma-enhanced chemical vapor deposition and depositing a layer of hydrogenated amorphous carbon on the hydrogenated amorphous silicon nitride layer by plasma-enhanced chemical vapor deposition. A subject matter of the invention is the use of the polyolefin container coated with a gas barrier coating for the storage of food or beverage materials.
1. A polyolefin container coated with a gas barrier coating comprising a first layer of hydrogenated amorphous silicon nitride and a second layer of hydrogenated amorphous carbon, the hydrogenated amorphous silicon nitride layer being deposited on the container, and the hydrogenated amorphous carbon layer being deposited on the hydrogenated amorphous silicon nitride layer.
2. A polyolefin container according to claim 1 wherein the gas barrier coating has a thickness of between 2 nm and 25 nm.
3. A polyolefin container according to claim 1 wherein at least 99% of the internal surface and/or at least 99% of the external surface of the polyolefin container is coated with the gas barrier coating.
4. A polyolefin container according to claim 1 wherein the container is injection-moulded.
5. A polyolefin container according to claim 1 wherein the polyolefin is polypropylene.
6. A polyolefin container according to claim 1 having an oxygen transfer rate per m 2 of container surface of less than 6 cm 3 of oxygen per day at 1 bar pressure and 100% oxygen.
7. A polyolefin container according to claim 1 wherein the container is closed by a membrane sealed to the container in a gas and moisture tight manner.
8. A polyolefin container according to claim 1 wherein the container is selected from the group consisting of a bottle, a tray, a cup and a capsule.
9. A process for coating a polyolefin container comprising the steps:
depositing a layer of hydrogenated amorphous silicon nitride on a polyolefin container by plasma-enhanced chemical vapor deposition; and
depositing a layer of hydrogenated amorphous carbon on the hydrogenated amorphous silicon nitride layer by plasma-enhanced chemical vapor deposition.
10. A process according to claim 9 wherein the hydrogenated amorphous silicon nitride layer is deposited by plasma-enhanced chemical vapor deposition of a mixture of silane and nitrogen.
11. A process according to claim 9 wherein the hydrogenated amorphous carbon layer is deposited by plasma-enhanced chemical vapor deposition of ethyne.
12. A process according to claim 9 further comprising pre-treating the polyolefin container with a plasma of argon before deposition of the hydrogenated amorphous silicon nitride layer.
13. A method of storing food or beverage comprising placing the food or beverage in a polyolefin container coated with a gas barrier coating comprising a first layer of hydrogenated amorphous silicon nitride and a second layer of hydrogenated amorphous carbon, the hydrogenated amorphous silicon nitride layer being deposited on the container, and the hydrogenated amorphous carbon layer being deposited on the hydrogenated amorphous silicon nitride layer.
14. A method for containing portioned ingredients for the preparation of a beverage by means of a beverage preparation machine comprising placing the ingredients in a polyolefin container coated with a gas barrier coating comprising a first layer of hydrogenated amorphous silicon nitride and a second layer of hydrogenated amorphous carbon, the hydrogenated amorphous silicon nitride layer being deposited on the container, and the hydrogenated amorphous carbon layer being deposited on the hydrogenated amorphous silicon nitride layer.
15. A method for providing a film-sealed food tray comprising using a polyolefin container coated with a gas barrier coating comprising a first layer of hydrogenated amorphous silicon nitride and a second layer of hydrogenated amorphous carbon, the hydrogenated amorphous silicon nitride layer being deposited on the container, and the hydrogenated amorphous carbon layer being deposited on the hydrogenated amorphous silicon nitride layer.