Aluminum-alloy brazing sheet
A brazing sheet for brazing in an inert-gas atmosphere without using a flux has a core and a filler material clad to one side or both sides of the core. The core has a chemical composition that contains Mg: 0.35-0.8% (mass %; likewise hereinbelow), the remainder being composed of Al and unavoidable impurities. The filler material has a chemical composition that contains Si: 6-13% and Bi: 0.001-0.05% and Mg: limited less than 0.05%, the remainder being composed of Al and unavoidable impurities.
1. An aluminum-alloy brazing sheet for brazing in an inert-gas atmosphere without using a flux, consisting of a core and a filler material clad to one side or both sides of the core, wherein:
the core has a chemical composition consisting of Mg: 0.35-0.8% (mass %; likewise hereinbelow)), and Si: 0.25% or less, Cu: 0.8% or less, Mn: 1.8% or less, Fe: 1.0% or less, Cr: 0.35% or less, Zn: 0.4% or less, and Ti: 0.10% or less, the remainder being Al and unavoidable impurities;
the filler material has a chemical composition consisting of Si: 6-13% and Bi: 0.001-0.05%, Zn: 5.0% or less, and Mg: 0.01% or less, the remainder being Al and unavoidable impurities; and
the filler material is an outermost layer of the aluminum-alloy brazing sheet.
2. The aluminum-alloy brazing sheet according to claim 1 , wherein the filler material further contains Zn: 0.1-5.0%.
3. The aluminum-alloy brazing sheet according to claim 1 , wherein the core contains at least one element selected from the group consisting of Cu: 0.05-0.8% and Mn: 0.01-1.8%.
4. The aluminum-alloy brazing sheet according to claim 1 , wherein the core contains at least one from among Si: 0.1-0.25%, Fe: 0.3-1.0%, Cr: 0.01-0.35%, Zn: 0.01-0.4%, and Ti: 0.01-0.10%.
5. The aluminum-alloy brazing sheet according to claim 1 , wherein the filler material has a thickness of 10-100 μm.
6. The aluminum-alloy brazing sheet according to claim 1 , wherein the core has a thickness of 330-390 μm.
7. The brazing sheet according to claim 1 , wherein the filler material contains Bi: 0.001-0.02%.
8. An aluminum-alloy brazing sheet for brazing in an inert-gas atmosphere without using a flux, consisting of a core and a filler material clad to one side or both sides of the core, wherein:
the core has a chemical composition consisting of Mg: 0.35-0.8% (mass %; likewise hereinbelow), Si: 0.25% or less, Cu: 0.8% or less, Mn: 1.8% or less, Fe: 1.0% or less, Cr: 0.35% or less, Zn: 0.4% or less, and Ti: 0.10% or less, the remainder being Al and unavoidable impurities;
the filler material has a chemical composition consisting of Si: 6-13%, Bi: 0.001-0.05%, Zn: 5.0% or less, Mg: 0.01% or less, Be: less than 0.001%, Ca: less than 0.01%, Li: less than 0.004%, Na: less than 0.001%, Y: less than 0.01%, La: less than 0.01%, and Ce: less than 0.01%, the remainder being Al and unavoidable impurities; and
the filler material is an outermost layer of the aluminum-alloy brazing sheet.
9. The aluminum-alloy brazing sheet according to claim 8 , wherein the filler material contains Zn: 0.1-5.0%.
10. The aluminum-alloy brazing sheet according to claim 8 , wherein the core contains at least one from among Cu: 0.05-0.8% and Mn: 0.01-1.8%.
11. The aluminum-alloy brazing sheet according to claim 8 , wherein the core contains at least one from among Si: 0.1-0.25%, Fe: 0.3-1.0%, Cr: 0.01-0.35%, Zn: 0.01-0.4%, and Ti: 0.01-0.10%.
12. The aluminum-alloy brazing sheet according to claim 8 , wherein the core and the filler material are configured such that the Mg concentration of an exterior surface of the filler material of the brazing sheet, after the temperature has been raised from 450° C. to 577° C. in 5-7 min and a cooling process has been subsequently performed, is less than 0.5 mass %.
13. The aluminum-alloy brazing sheet according to claim 9 , wherein the core contains at least one element selected from the group consisting of Cu: 0.05-0.8% and Mn: 0.01-1.8%.
14. The aluminum-alloy brazing sheet according to claim 13 , wherein the core contains at least one from among Si: 0.1-0.25%, Fe: 0.3-1.0%, Cr: 0.01-0.35%, Zn: 0.01-0.4%, and Ti: 0.01-0.10%.
15. The aluminum-alloy brazing sheet according to claim 14 , wherein the filler material has a thickness of 10-100 μm.
16. The aluminum-alloy brazing sheet according to claim 14 , wherein the filler material has a thickness of 60-100 μm.
17. The aluminum-alloy brazing sheet according to claim 14 , wherein the core has a thickness of 330-390 μm.
18. The brazing sheet according to claim 8 , wherein the filler material contains Bi: 0.001-0.02%.
19. A brazing sheet consisting of one of:
a first metallic layer clad to one outer side of a second metallic layer; or
a first metallic layer clad to both outer sides of a second metallic layer;
wherein:
the second metallic layer is a core composed of an aluminum alloy consisting of Mg: 0.35-0.8% (mass %; likewise hereinbelow), and Si: 0.25% or less Cu: 0.8% or less, Mn: 1.8% or less, Fe: 1.0% or less, Cr: 0.35% or less, Zn: 0.4% or less, Ti: 0.10% or less, and unavoidable impurities; and
the first metallic layer is a filler material composed of an aluminum alloy consisting of Si: 6-13% Bi: 0.001-0.05% Zn: 5.0% or less, Mg: 0.01% or less, and unavoidable impurities.
20. The brazing sheet according to claim 19 , wherein the filler material contains Zn: 0.1-5.0%.
21. The brazing sheet according to claim 19 , wherein the core contains at least one element selected from the group consisting of Cu: 0.05-0.8% and Mn: 0.01-1.8%.
22. The brazing sheet according to claim 19 , wherein the core contains at least one from among Si: 0.1-0.25%, Fe: 0.3-1.0%, Cr: 0.01-0.35%, Zn: 0.01-0.4%, and Ti: 0.01-0.10%.
23. The brazing sheet according to claim 19 , wherein the filler material contains Bi: 0.001-0.02%.