Promoted, attrition resistant, silica supported precipitated iron catalyst
A structurally promoted precipitated catalyst containing crystalline silica, at least one chemical promoter selected from the group consisting of alkali metals, and iron, the structurally promoted precipitated catalyst comprising maghemite and hematite catalytic phases, and exhibiting a main reduction peak temperature, as determined by TPR, in the range of from about 210° C. to about 350° C. A method of producing the structurally promoted precipitated catalyst is also provided.
1. A structurally promoted precipitated catalyst comprising:
crystalline silica;
at least one chemical promoter selected from the group consisting of alkali metals; and
iron;
wherein the structurally promoted precipitated catalyst comprises maghemite and hematite catalytic phases, and wherein the structurally promoted precipitated catalyst has a main reduction peak temperature, as determined by TPR, in the range of from about 210° C. to about 350° C.; and wherein the structurally promoted precipitated catalyst comprises a substantially homogeneous distribution of iron and alkali metal due to production thereof via impregnation of a precipitated iron catalyst slurry with an alkali-silicate support solution consisting essentially of:
crystalline silica dissolved in an aqueous solution comprising at least one chemical promoter selected from the group consisting of alkali metal bases.
2. The structurally promoted precipitated catalyst of claim 1 , wherein the alkali-silicate support solution has a pH of greater than or equal to about 7.
3. The structurally promoted precipitated catalyst of claim 1 , wherein the chemical promoter comprises an alkali hydroxide.
4. The structurally promoted precipitated catalyst of claim 3 , wherein the chemical promoter is selected from the group consisting of sodium hydroxide, potassium hydroxide, and combinations thereof.
5. The structurally promoted precipitated catalyst of claim 4 , wherein the chemical promoter comprises potassium hydroxide.
6. The structurally promoted precipitated catalyst of claim 1 , wherein the alkali-silicate support solution further comprises a structural support selected from the group consisting of boehmite, amorphous silica, silicic acid, tetraethyl orthosilicate, alumina, MgAl 2 O 4 and combinations thereof.
7. The structurally promoted precipitated catalyst of claim 1 , wherein the alkali-silicate support solution comprises no significant concentration of salt.
8. The structurally promoted precipitated catalyst of claim 1 comprising SiO 2 :Fe in a weight ratio of from about 2:100 to about 24:100.
9. The structurally promoted precipitated catalyst of claim 8 further comprising copper.
10. The structurally promoted precipitated catalyst of claim 9 , wherein the catalyst comprises a weight ratio of Cu: Fe in the range of from 1:100 to about 10:100.
11. The structurally promoted precipitated catalyst of claim 10 , wherein the catalyst comprises K:Fe in a weight ratio of from about 1:100 to about 10:100.
12. The structurally promoted precipitated catalyst of claim 1 having an ASTM air jet attrition resistance such that less than about 5 wt % fines are produced within a testing duration of 5 hours.
13. The structurally promoted precipitated catalyst of claim 12 , wherein less than 1 wt % fines are produced within a testing duration of 5 hours.
14. The structurally promoted precipitated catalyst of claim 1 , wherein the catalyst catalyzes Fischer-Tropsch synthesis.
15. The structurally promoted precipitated catalyst of claim 1 having a main reduction peak temperature, as determined by TPR, in the range of from about 210° C. to about 280° C.
16. The structurally promoted precipitated catalyst of claim 1 comprising substantially no iron silicates.
17. The structurally promoted precipitated catalyst of claim 1 exhibiting substantially equivalent x-ray diffraction peaks for maghemite and hematite.