Process for treating a sulfurous fluid to form gypsum and magnesium carbonate
A process for treating a sulfurous fluid to form gypsum and magnesium carbonate, whereby the sulfurous fluid is scrubbed with a sequestrating agent to yield a scrubbed fluid, gypsum and magnesium sulfate. The flue gas desulfurized gypsum is isolated from the magnesium sulfate solution by filtration or centrifugation. The magnesium sulfate is reacted with a carbonate salt to produce a magnesium carbonate whereby the reaction conditions are controlled to control the properties of the magnesium carbonate produced.
1. A process for treating a sulfurous fluid to form gypsum and magnesium carbonate, comprising:
contacting the sulfurous fluid with a sequestrating agent to yield a scrubbed fluid, gypsum and magnesium sulfate; and
reacting a carbonate salt with the magnesium sulfate to produce a magnesium carbonate; wherein the carbonate salt comprises a carbonate anion and at least one cation selected from the group consisting of sodium, calcium, potassium, ammonium, magnesium, and hydronium.
2. The process of claim 1 , further comprising separating at least a portion of the gypsum from the magnesium sulfate to form a gypsum product.
3. The process of claim 2 , wherein the separating is by filtration or centrifugation.
4. The process of claim 2 , wherein the moisture content of the gypsum product after separating does not exceed 10%.
5. The process of claim 2 , wherein the gypsum product comprises at least one impurity selected from the group consisting of a carbonate, a sulfate, an iron mineral, and an organic species.
6. The process of claim 1 , wherein the sequestrating agent is a calcium-containing carbonate mineral.
7. The process of claim 6 , wherein the calcium-containing carbonate material is dolomite or dolomitic limestone.
8. The process of claim 6 , wherein the calcium-containing carbonate mineral has an average particle size ranging from 50 μm to 100 μm.
9. The process of claim 1 , wherein the sulfurous fluid is a flue gas with a temperature ranging from 350° C. to 1200° C.
10. The process of claim 1 , wherein the contacting removes 98 to 99% of sulfur from the sulfurous fluid.
11. The process of claim 1 , further comprising flowing a sulfurous fluid into a mixture comprising water and a sequestrating agent, wherein the pH of the mixture is controlled during the flowing by controlling a flow rate of the sulfurous fluid into the mixture, adding a buffer to the mixture, or both.
12. The process of claim 11 , wherein the buffer is ammonia, a dibasic acid, or both.
13. The process of claim 11 , wherein the mixture has a pH from 5 to 6 during the flowing.
14. The process of claim 11 , further comprising flowing oxygen into the mixture concurrently with the sulfurous fluid to reduce a concentration of sulfites in the mixture.
15. The process of claim 1 , wherein the magnesium carbonate is amorphous with a surface area greater than or equal to 20 m2/g.
16. The process of claim 1 , further comprising seeding the magnesium sulfate prior to the reacting by adding gypsum, a carbonate salt seed, or both to control the production of the magnesium carbonate.
17. The process of claim 1 , wherein said magnesium carbonate is in the form magnesite.
18. The process of claim 1 , further comprising: separating at least a portion of the gypsum from the magnesium sulfate to form a gypsum product; and processing the gypsum to form a processed gypsum.
19. The process of claim 18 , wherein the processing is at least one process selected from the group consisting of grinding, milling, recrystallizing, magnetically separating, bleaching, acid washing, and beneficiating.
20. The process of claim 18 , wherein the processed gypsum is 90 to 99% pure gypsum.