Composition for non-aqueous secondary battery functional layer, non-aqueous secondary battery functional layer, and non-aqueous secondary battery

1. A composition for a non-aqueous secondary battery functional layer, comprising:

non-conductive inorganic particles selected from a group consisting of particles of oxides, particles of nitrides, particles of covalent crystals, particles of hardly-soluble ionic crystals, microparticles of days, and a mixture thereof, and

organic particles,

wherein a difference in density between the non-conductive inorganic particles and the organic particles calculated by subtracting a density of the organic particles from a density of the non-conductive inorganic particles is 1.5 g/cm 3 or more,

at least a surface layer portion of the organic particles is made of a first polymer containing an aromatic vinyl monomer unit and an acid group-containing monomer unit, the first polymer having a degree of swelling in electrolysis solution of greater than 1 time to 4 times and having a glass-transition temperature of 50° C. or above,

the organic particles have a core-shell structure that comprises a core and a shell that partially covers an outer surface of the core, wherein the shell is made of the first polymer and the core is made of a second polymer containing a (meth)acrylic acid ester monomer unit, an acid group-containing monomer unit, and a cross-linkable monomer unit, the second polymer having a degree of swelling in electrolysis solution of 5 times to 30 times, and

a volume-average particle diameter of the organic particles is 0.80 to LSO times a volume-average particle diameter of the non-conductive inorganic particles,

wherein a blending ratio of the organic particles to the non-conductive inorganic particles is 1 part by mass to 20 parts by mass with respect to 100 parts by mass of the non-conductive inorganic particles,

wherein the shell of the core-shell structure has an average thickness in percentage relative to the volume-average particle diameter of the organic particles of 1% or more and 30% or less,

wherein the degree of swelling of the first polymer in electrolysis solution is determined by comparison of weights of a 1 cm×1 cm square sheet of the polymer having a thickness of 0.5 mm before and after immersing the square sheet in the electrolysis solution at 60° C. for 72 hours, and

wherein the degree of swelling of the second polymer in electrolysis solution is determined by comparison of weights of a 1 cm×1 cm square sheet of the second polymer having a thickness of 0.5 mm before and after immersing the square sheet in the electrolysis solution at 60° C. for 72 hours.

2. The composition for a non-aqueous secondary battery functional layer of claim 1 , wherein the volume-average particle diameter of the non-conductive inorganic particles is 0.1 μm to 2 μm.

3. The composition for a non-aqueous secondary battery functional layer of claim 1 , wherein the volume-average particle diameter of the organic particles is 0.5 μm to 3 μm.

4. The composition for a non-aqueous secondary battery functional layer of claim 1 , further comprising a particulate polymer having a glass-transition temperature of 20° C. or below.

5. The composition for a non-aqueous secondary battery functional layer of claim 4 , wherein a volume-average particle diameter of the particulate polymer is 0.01 times to 0.60 times the volume-average particle diameter of the non-conductive inorganic particles.

6. A non-aqueous secondary battery functional layer formed using the composition for a non-aqueous secondary battery functional layer of claim 1 .

7. A non-aqueous secondary battery comprising the non-aqueous secondary battery functional layer of claim 6 .