Method for bonding wafers
Provided is a method for bonding wafers, which can bond the wafers to each other with high reliability while reducing the influence on the wafers. The method for bonding wafers includes the steps of: preparing a first wafer that has, on the surface thereof, a first metal layer with a first rigidity modulus, and a second wafer that has, on the surface thereof, a second metal layer with a second rigidity modulus higher than the first rigidity modulus; removing an oxide film at the surface of the second metal layer while an oxide film at the surface of the first metal layer is not removed; and bonding the surface of the first wafer to the surface of the second wafer.
1. A method for bonding wafers, the method comprising:
preparing a first wafer having a first metal layer with a first rigidity modulus, the first metal layer being formed from an aluminum-copper alloy, the percentage of copper in the aluminum-copper alloy by weight being 1 wt % or less, aluminum being the main constituent of the first metal layer;
preparing a second wafer having a second metal layer with a second rigidity modulus higher than the first rigidity modulus, the second metal layer being formed from a second metal containing germanium as its main constituent;
removing a first oxide film on a first surface of the second metal layer while not removing a second oxide film on a second surface of the first metal layer; and
bonding the first surface of the second metal layer to the second surface of the first metal layer in such a manner that the oxide film on the second surface of the first metal layer is broken due to mechanical shock.
2. A method for bonding wafers, the method comprising:
preparing a first wafer having a first metal layer with a first rigidity modulus, the first metal being formed of an aluminum-copper alloy, the percentage of copper by weight in the aluminum-copper alloy by weight being 1% or less, aluminum being the main constituent of the first metal layer, the first metal being one of an alloy of aluminum and copper and an alloy of aluminum, silicon and copper;
preparing a second wafer having a second metal layer with a second rigidity modulus higher than the first rigidity modulus, the second metal layer is formed of a metal containing germanium;
removing a first oxide film on a first surface of the second metal layer while not removing a second oxide film on a second surface of the first metal layer; and
bonding the first surface of the second metal layer to the second surface of the first metal layer in such a manner that the oxide film on the second surface of the first metal layer is broken due to mechanical shock.