Dip-formed synthetic polyisoprene latex articles with improved intraparticle and interparticle crosslinks
A synthetic polyisoprene latex emulsion has pre-vulcanization composition and post vulcanization composition. The pre-vulcanization composition comprises soluble sulfur with high S 8 ring structure that is catalytically broken by a zinc dithiocarbamate. Surfactants present in the pre-vulcanization composition wets synthetic polyisoprene particles and permeates small sized sulfur and accelerator molecules into the interior of these particles thereby pre-vulcanizing the particles. The degree of pre-vulcanization is verified by isopropanol index test. The latex emulsion has post-vulcanization composition with accelerators that crosslink inter-particle region during post vulcanization cure cycle. The dipped synthetic polyisoprene article is substantially uniformly cured both in the inter-particle and intra-particle regions and reliably exhibits high cross link density, uniform distribution of double bonds in TEM and zinc segregation at the boundaries or original particles by electron microprobe analysis. The films exhibit high tensile strength, tensile modulus, tear strength, burst pressure and burst volume.
1. A synthetic polyisoprene elastomeric glove or condom made of a layer of elastomer comprising:
a plurality of synthetic polyisoprene particles that are pre-vulcanized and cured, each synthetic polyisoprene particle having intra-polyisoprene particle crosslinks distributed within the synthetic polyisoprene particle, and wherein the plurality of synthetic polyisoprene particles are crosslinked to each other through a network of inter-particle crosslinks.
2. A synthetic polyisoprene elastomeric glove or condom made of a layer of elastomer comprising:
a plurality of synthetic polyisoprene particles that are pre-vulcanized and cured, each synthetic polyisoprene particle having intra-polyisoprene particle crosslinks distributed within the synthetic polyisoprene particle, and wherein the plurality of synthetic polyisoprene particles are crosslinked to each other through a network of inter-particle crosslinks, wherein the synthetic polyisoprene elastomeric glove or condom has an elongation at break of about 750% or more.
3. A synthetic polyisoprene elastomeric condom made of a layer of elastomer wherein a middle portion of the layer shows a network of synthetic polyisoprene particles that are pre-vulcanized and cured abutting each other at intersections after being infused and swollen with styrene, and after the infused styrene is crosslinked, wherein the condom shows one or more of the following properties:
tensile strength of about 30 Mpa or higher by ISO 4074:2002;
elongation at break of about 800% or higher by ISO 4074:2002;
mean burst volume of about 40 L or higher by ASTM D624:2000; or
mean burst pressure of about 1.4 kPa or higher by ASTM D624:2000.