Methods for forming transistor gates with hafnium oxide layers and lanthanum oxide layers
A method includes forming a gate stack of a transistor. The formation of the gate stack includes forming a silicon oxide layer on a semiconductor region, depositing a hafnium oxide layer over the silicon oxide layer, depositing a lanthanum oxide layer over the hafnium oxide layer, and depositing a work-function layer over the lanthanum oxide layer. Source/drain regions are formed on opposite sides of the gate stack.
1. A method comprising:
forming a first gate stack of a first transistor comprising:
forming a silicon oxide layer on a semiconductor region;
depositing a hafnium oxide layer over the silicon oxide layer;
depositing a lanthanum oxide layer over the hafnium oxide layer;
depositing a lanthanum silicon oxide layer over the lanthanum oxide layer;
depositing a work-function layer over the lanthanum silicon oxide layer; and
forming first source/drain regions on opposite sides of the first gate stack.
2. The method of claim 1 further comprising depositing a hafnium silicate layer between the silicon oxide layer and the hafnium oxide layer.
3. The method of claim 2 , wherein the hafnium silicate layer has a hafnium atomic percentage lower than about 10 percent.
4. The method of claim 1 , wherein at a time before the hafnium oxide layer is deposited and after the silicon oxide layer is formed, the silicon oxide layer is free from hafnium.
5. The method of claim 1 further comprising:
removing the lanthanum oxide layer and the hafnium oxide layer; and
depositing another hafnium oxide layer over the silicon oxide layer.
6. The method of claim 1 further comprising depositing a titanium silicon nitride layer over the lanthanum oxide layer.
7. A method comprising:
forming a silicon oxide layer comprising a first portion and a second portion over a first semiconductor region and a second semiconductor region, respectively;
depositing a first hafnium oxide layer comprising a first portion and a second portion over the first portion and the second portion, respectively, of the silicon oxide layer;
depositing a lanthanum oxide layer comprising a first portion and a second portion over the first portion and the second portion, respectively, of the first hafnium oxide layer;
removing the second portion of the lanthanum oxide layer and the second portion of the first hafnium oxide layer;
depositing a second hafnium oxide layer over the second portion of the silicon oxide layer; and
depositing a first work function layer over the first portion of the lanthanum oxide layer and a second work function layer over the second hafnium oxide layer, respectively.
8. The method of claim 7 further comprising:
forming n-type source/drain regions on opposite sides of the first work function layer; and
forming p-type source/drain regions on opposite sides of the second work function layer.
9. The method of claim 7 further comprising depositing a titanium silicon nitride layer comprising:
a first portion over the first portion of the lanthanum oxide layer; and
a second portion over and in contact with the second hafnium oxide layer.
10. The method of claim 7 further comprising:
depositing a lanthanum silicon oxide layer comprising a first portion and a second portion over the first portion and the second portion, respectively, of the lanthanum oxide layer; and
removing the second portion of the lanthanum silicon oxide layer.
11. The method of claim 7 further comprising:
depositing a hafnium silicate layer comprising a first portion and a second portion over the first portion and the second portion of the silicon oxide layer, respectively; and
removing the second portion of the hafnium silicate layer.
12. The method of claim 11 , wherein the hafnium silicate layer has a hafnium atomic percentage lower than about 10 percent.
13. The method of claim 7 further comprising performing an anneal on the lanthanum oxide layer and the first hafnium oxide layer.
14. A method comprising:
forming a gate stack of a transistor, the forming the gate stack comprising:
forming a silicon oxide layer on a semiconductor region;
depositing a hafnium oxide layer over the silicon oxide layer;
depositing a lanthanum oxide layer over the hafnium oxide layer;
removing the lanthanum oxide layer; and
forming a source/drain region on a side of the gate stack.
15. The method of claim 14 further comprising depositing a hafnium silicate layer over the silicon oxide layer, wherein the hafnium oxide layer is deposited over the hafnium silicate layer.
16. The method of claim 14 further comprising removing the hafnium oxide layer.
17. The method of claim 14 further comprising annealing the lanthanum oxide layer.
18. The method of claim 17 further comprising depositing a work-function layer, wherein the annealing is performed before the work-function layer is deposited.
19. The method of claim 16 further comprising, after the lanthanum oxide layer and the hafnium oxide layer are removed, forming a high-k dielectric layer over and contacting the silicon oxide layer.
20. The method of claim 2 , wherein the hafnium silicate layer contacts both of the silicon oxide layer and the hafnium oxide layer.