Method of quasi atomic layer etching
Techniques herein include an etch process that etches a layer of material incrementally, similar to mono-layer etching of atomic layer etching (ALE), but not necessarily including self-limiting, mono-layer action of ALE. Such techniques can be considered as quasi-atomic layer etching (Q-ALE). Techniques herein are beneficial to precision etching applications such as during soft-mask open. Techniques herein enable precise transfer of a given mask pattern into an underlying layer. By carefully controlling the polymer deposition relative to polymer assisted etching through its temporal cycle, a very thin layer of conformal polymer can be activated and used to precisely etch and transfer the desired patterns.
1. A method of processing a substrate, the method comprising:
receiving a substrate having a working surface, the working surface having a relief pattern formed on an underlying layer such that portions of the underlying layer are uncovered;
executing a conformal film deposition process that conformally deposits a polymer film on the substrate, wherein the polymer film has a thickness of less than three nanometers;
executing an activation etch process that etches the underlying layer using the polymer film until the polymer film is removed from horizontal surfaces of the underlying layer that are parallel to the working surface; and
cycling steps of conformal film deposition and activation etch until removing a predetermined amount of the underlying layer that is uncovered by the relief pattern,
wherein executing the conformal film deposition includes maintaining plasma at a first ion energy, and wherein executing the activation etch process includes maintaining plasma at a second ion energy, the second ion energy is greater than the first ion energy, and the first ion energy is below a threshold energy sufficient for activating etching of a particular deposition material and ion combination.
2. The method of claim 1 , wherein the relief pattern is comprised of photoresist material.
3. The method of claim 2 , wherein the photoresist material is EUV photoresist.
4. The method of claim 1 , wherein the underlying layer is a soft-mask material.
5. The method of claim 1 , wherein executing the conformal film deposition process includes using an isotropic deposition process, and wherein executing the activation etch process includes using an anisotropic etch process.
6. The method of claim 1 , wherein executing the activation etch process includes coupling low-frequency bias power to a plasma processing chamber.
7. The method of claim 1 , wherein executing the conformal film deposition includes depositing the polymer film for 1-9 seconds, and wherein executing the activation etch process includes anisotropically etching the underlying layer for 3-9 seconds.
8. The method of claim 1 , wherein executing the conformal film deposition includes controlling a degree of conformality by selectively using continuous wave plasma or pulsed plasma based on iso-dense characteristics of a working surface of the substrate.
9. A method of processing a substrate, the method comprising:
receiving a substrate having a working surface, the working surface having a relief pattern formed on an underlying layer such that portions of the underlying layer are uncovered;
executing a conformal film deposition process that conformally deposits a polymer film on the substrate, wherein the polymer film has a thickness of less than three nanometers;
executing an activation etch process that etches the underlying layer using the polymer film until the polymer film is removed from horizontal surfaces of the underlying layer that are parallel to the working surface; and
cycling steps of conformal film deposition and activation etch until removing a predetermined amount of the underlying layer that is uncovered by the relief pattern wherein executing the conformal film deposition includes using a C x F y process gas, and wherein executing the activation etch process includes stopping flow of the C x F y process gas.
10. A method of processing a substrate, the method comprising:
receiving a substrate having a working surface, the working surface having a relief pattern formed on an underlying layer such that portions of the underlying layer are uncovered;
executing a conformal film deposition process that conformally deposits a polymer film on the substrate, wherein the conformal film deposition process is executed for 1-9 seconds;
executing an activation etch process that etches the underlying layer for 3-9 seconds using the polymer film; and
cycling steps of conformal film deposition and activation etch until removing a predetermined amount of the underlying layer,
wherein executing the conformal film deposition includes maintaining plasma at a first plasma density, and wherein executing the activation etch process includes maintaining plasma at a second plasma density, wherein the first plasma density is greater than the second plasma density.
11. The method of claim 10 , wherein relief pattern is a soft-mask material.
12. The method of claim 10 , wherein executing the conformal film deposition process includes using an isotropic deposition process, and wherein executing the activation etch process includes using an anisotropic etch process.
13. The method of claim 10 , wherein executing the activation etch process includes coupling low-frequency bias power to a plasma processing chamber.
14. A method of processing a substrate, the method comprising:
receiving a substrate having a working surface, the working surface having a relief pattern formed on an underlying layer such that portions of the underlying layer are uncovered;
executing a conformal film deposition process that conformally deposits a polymer film on the substrate, wherein the conformal film deposition process is executed for 1-9 seconds;
executing an activation etch process that etches the underlying layer for 3-9 seconds using the polymer film; and
cycling steps of conformal film deposition and activation etch until removing a predetermined amount of the underlying layer, wherein executing the conformal film deposition includes using a C x F y process gas, and wherein executing the activation etch process includes stopping flow of the C x F y process gas.
15. A method of processing a substrate, the method comprising:
receiving a substrate having a working surface, the working surface having a relief pattern formed on an underlying layer such that portions of the underlying layer are uncovered;
executing a conformal film deposition process that conformally deposits a polymer film on the substrate, wherein the polymer film has a thickness of less than three nanometers;
executing an activation etch process that etches the underlying layer using the polymer film until the polymer film is removed from horizontal surfaces of the underlying layer that are parallel to the working surface, wherein the polymer film is activated by an ion energy to react with material of the underlying layer to remove a portion of the underlying layer; and
cycling steps of conformal film deposition and activation etch until removing a predetermined amount of the underlying layer that is uncovered by the relief pattern.
16. The method of claim 15 , wherein executing the conformal film deposition includes maintaining plasma at a first ion energy below a threshold energy sufficient for activating etching based on a particular combination of deposited polymer film and ion, and wherein executing the activation etch process includes maintaining plasma at a second ion energy, wherein the second ion energy is greater than the first ion energy.
17. The method of claim 15 , wherein executing the conformal film deposition includes using a C x F y process gas, and wherein executing the activation etch process includes stopping flow of the C x F y process gas.