Nucleated polyethylene blends and their use in molded articles

1. A polyethylene blend comprising from 5 to 95 weight percent of a polyethylene homopolymer composition, and from 95 to 5 weight percent of a bimodal polyethylene copolymer; wherein the polyethylene homopolymer composition comprises a nucleating agent or mixture of nucleating agents; and wherein the polyethylene homopolymer composition comprises (I) 5 to 70 weight percent of a first ethylene homopolymer having a density of from 0.950 to 0.975 g/cm 3 ; and (II) 95 to 30 weight percent of a second ethylene homopolymer having a density of from 0.950 to 0.975 g/cm 3 , wherein the ratio of the melt index I 2 of the second ethylene homopolymer to the melt index I 2 of the first ethylene homopolymer is at least 10.

2. The polyethylene blend of claim 1 , wherein the bimodal polyethylene copolymer comprises (III) 10 to 70 weight percent of a first ethylene copolymer having a melt index, 12, of less than 0.4 g/10 min and a density of from 0.925 to 0.950 g/cm 3 ; and (IV) 90 to 30 weight percent of a second ethylene copolymer having a melt index I 2 , of from 100 to 20,000 g/10 min and a density higher than the density of the first ethylene copolymer, but less than 0.967 g/cm 3 ;

wherein the density of the second ethylene copolymer is less than 0.037 g/cm 3 higher than the density of the first ethylene copolymer; and the ratio (SCB1/SCB2) of the number of short chain branches per thousand carbon atoms in the first ethylene copolymer (SCB1) to the number of short chain branches per thousand carbon atoms in the second ethylene copolymer (SCB2) is greater than 0.5.

3. The polyethylene blend of claim 2 , wherein the polyethylene blend has a bimodal profile in a gel permeation chromatograph.

4. The polyethylene blend of claim 2 , wherein the polyethylene blend has a density of from 0.951 to 0.971 g/cm 3 .

5. The polyethylene blend of claim 2 , wherein the polyethylene blend has a melt index, I 2 of from 1.0 to 10.0 g/10 min.

6. The polyethylene blend of claim 2 , wherein the polyethylene blend has a molecular weight distribution M W /M N of from 3.0 to 13.0.

7. The polyethylene blend of claim 2 , wherein the polyethylene blend comprises from 20 to 80 weight percent of the polyethylene homopolymer composition, and from 80 to 20 weight percent of a bimodal polyethylene copolymer.

8. The polyethylene blend of claim 2 , wherein the polyethylene blend comprises from about 10 to 60 weight percent of the polyethylene homopolymer composition and from 90 to 40 weight percent of the bimodal polyethylene copolymer.

9. The polyethylene blend of claim 2 , wherein the nucleating agent or mixture of nucleating agents comprises a salt of a dicarboxylic acid.

10. The polyethylene blend of claim 2 , wherein the ethylene homopolymer composition comprises from 100 to 3,000 ppm of the nucleating agent or mixture of nucleating agents.

11. A compression molded article comprising the polyethylene blend of claim 1 .

12. A compression molded article comprising the polyethylene blend of claim 2 .

13. An injection molded article comprising the polyethylene blend of claim 1 .

14. An injection molded article comprising the polyethylene blend of claim 2 .

15. A closure comprising the polyethylene blend of claim 1 .

16. A closure comprising the polyethylene blend of claim 2 .

17. A film comprising the polyethylene blend of claim 1 .

18. A film comprising the polyethylene blend of claim 2 .