Flexible magnetic sheet, and method of making
Adhering systems for magnetizable laminates to assist preventing delamination of magnetizable laminates exposed to direct sunlight; and, relating to preventing fouling of cutting blades during cutting of magnetizable laminates.
1. A flexible magnetic sheet comprising:
a magnetizable layer comprising at least one magnetizable component and at least one binder, the magnetizable layer is configured to be magnetizable so as to be useful in magnetically adhering the flexible magnetic sheet to a magnetically receptive surface;
an opaque white or colored writeable outer layer located on one side of the flexible magnetic sheet;
a moisture cured adhesive layer destructively bonding the magnetizable layer and the writeable outer layer together, the moisture cured adhesive layer having a thickness of about 0.6 mil to about 1.5 mil and comprising about 95% to about 99% polyurethane and about 1% to about 3% methylene bisphenyl isocyanate,
wherein the cured adhesive layer is formulated to be resistant to transfer from the flexible magnetic sheet to cutting blades during cutting of the flexible magnetic sheet,
wherein the flexible magnetic sheet is constructed to be resistant to delamination on exposure to direct sunlight, and
wherein cured adhesive of the cured adhesive layer is formulated to not be tacky when exposed to a cutting-machine operational temperature of about 110 degrees Fahrenheit or about 43 degrees Celsius, so as to transfer essentially no residue to the cutting blades.
2. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer is flexible at room temperature.
3. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer comprises at least one hot-melt adhesive.
4. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer comprises at least one reactive hot-melt adhesive.
5. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer comprises at least one virtually-thermosetable hot-melt adhesive.
6. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer comprises at least one thermoplastic hot-melt adhesive.
7. The flexible magnetic sheet according to claim 1 , wherein the writeable outer layer comprises synthetic paper.
8. The flexible magnetic sheet according to claim 7 , wherein the synthetic paper comprises a thickness of about 3.2 mil.
9. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer is formed from an adhesive composition that is solid.
10. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer is formed from an adhesive composition that is not solvent based.
11. The flexible magnetic sheet according to claim 1 , wherein adhesive of the moisture cured adhesive layer is formed from an adhesive composition comprising no volatile organic compound.
12. A flexible magnetic sheet comprising:
a magnetizable layer comprising at least one magnetizable component and at least one binder, the magnetizable layer is configured to be magnetizable so as to be useful in magnetically adhering the flexible magnetic sheet to a magnetically receptive surface;
an opaque white or colored writeable outer layer;
a moisture cured adhesive layer destructively bonding the magnetizable layer and the writeable outer layer together, the moisture cured adhesive layer having a thickness of about 0.6 mil to about 1.5 mil and comprising about 95% to about 99% polyurethane and about 1% to about 3% methylene bisphenyl isocyanate;
wherein the polyurethane used to form the adhesive layer has a viscosity of about 18,000 cP at about 82° C.,
wherein the cured adhesive layer is formulated to be resistant to transfer from the flexible magnetic sheet to cutting blades during cutting of the flexible magnetic sheet,
wherein the flexible magnetic sheet is constructed to be resistant to delamination on exposure to direct sunlight, and
wherein cured adhesive of the cured adhesive layer is formulated to not be tacky when exposed to a cutting-machine operational temperature of about 43 degrees Celsius, so as to transfer essentially no residue to the cutting blades.
13. A method of making a flexible magnetic sheet of claim 1 comprising at least three (3) continuous layers extending to edges of the flexible magnetic sheet, the method comprising:
providing a magnetizable layer, the magnetizable layer comprising at least one magnetizable component and at least one binder, the magnetizable layer is magnetizable so to be useful in magnetically adhering to a magnetically receptive surface;
providing an opaque white or colored writeable outer layer located on one side of the flexible magnetic sheet;
applying adhesive to the writeable outer layer to form an adhesive layer on the writeable outer layer, the adhesive layer having a thickness of about 0.6 mil to about 1.5 mil;
joining the adhesive layer of the writeable outer layer with the magnetizable layer; and curing the adhesive layer when located between the magnetizable layer and writeable outer layer,
wherein the cured adhesive layer is resistant to transfer from the flexible magnetic sheet to cutting blades during cutting of the flexible magnetic sheet,
wherein the flexible magnetic sheet is resistant to delamination on exposure to direct sunlight.
14. The method according to claim 13 , further comprising heating the adhesive prior to applying the adhesive to the writeable outer layer to form the adhesive layer on the writeable outer layer.
15. The method according to claim 14 , wherein the adhesive is heated to about 250 degrees Fahrenheit prior to applying the adhesive to the writeable outer layer to form the adhesive layer on the writeable outer layer.
16. The method according to claim 13 , wherein the adhesive layer is cooled after being applied to the writeable outer layer prior to joining the adhesive layer of the writeable outer layer with the magnetizable layer.
17. The method according to claim 13 , wherein the adhesive is applied to the writeable outer layer under pressure.
18. The method according to claim 17 , wherein the pressure is applied by at least one pressure roller.
19. The method according to claim 13 , wherein humidity of about 28 percent to about 70 percent is applied when curing the adhesive.
20. The flexible magnetic sheet according to claim 13 , wherein the cured adhesive layer, after being cured, is not tacky when exposed to a cutting-machine operational temperature of 110 degrees Fahrenheit, so as to transfer essentially no residue to the cutting blades.