Method for producing a plastic molded article, plastic molded article and mold

1. A method for producing a plastic molded article with the steps:

a) providing at least one base body made of a fiber composite plastic, wherein the fiber composite plastic comprises at least one sheet material ply made of continuous fibers and a plastic material impregnating the at least one sheet material ply, the base body being provided as a semi-finished product in sheet form having some of the continuous fibers of the at least one sheet material ply protruding beyond the plastic impregnation;

b) providing at least one decorative film;

c) heating the at least one base body;

d) joining at least one area of the at least one base body to the at least one decorative film in a mold, wherein a forming of the base body with the at least one decorative film in the mold is provided;

e) detaching a carrier ply from the at least one decorative film after the forming; and

f) injection molding at least one plastic structure onto the formed base body in the mold, whereby the plastic structure is molded around an edge area of the base body such that any of the protruding continuous fibers of the base body are enclosed by the plastic structure, and wherein the plastic structure comprises reinforcing elements, colorants and/or pigments.

2. The method according to claim 1 , wherein the at least one decorative film is provided as roll goods.

3. The method according to claim 2 , wherein the at least one decorative film is die-cut or cut before the forming.

4. The method according to claim 2 , wherein the at least one decorative film is die-cut in the mold.

5. The method according to claim 1 , wherein the base body is heated by infrared irradiation, contact heating, in a convection oven or inside the mold.

6. The method according to claim 1 , wherein the base body is heated to a temperature which is 0° C. to 100° C. higher than a melting point or a glass-transition temperature of a plastic matrix of the fiber composite plastic.

7. The method according to claim 1 , wherein the base body is heated to a temperature of from 100° C. to 300° C.

8. The method according to claim 1 , wherein the base body and the at least one decorative film are formed by hydraulic, pneumatic or electrical application of pressure between two halves of the mold.

9. The method according to claim 1 , wherein the mold is temperature-controlled.

10. The method according to claim 1 , wherein the mold is heated isothermally to a temperature of from 40° C. to 180° C.

11. The method according to claim 1 , wherein the mold is temperature-controlled variothermally, with a temperature control between 0K and 250K below the melting temperature of a polymer used, with a heating or cooling gradient of from 1K/s to 30K/s.

12. The method according to claim 1 , wherein the at least one decorative film is positioned in the mold with the aid of registration marks and/or stamped marks.

13. The method according to claim 1 , wherein the base body and/or the at least one decorative film are fixed in the mold by clamping devices and/or vacuum.

14. The method according to claim 1 , wherein, during the forming, a surface structure is introduced into the base body and/or into the plastic structure and/or into the at least one decorative film at least in areas.

15. The method according to claim 1 , wherein the molding is effected at a temperature of from 200° C. to 320° C.

16. The method according to claim 1 , wherein the molding is effected at a pressure of from 10 bar to 2000 bar.

17. The method according to claim 1 , wherein the plastic molded article, after the forming and/or injection molding, is cooled to a temperature of from 150° C. to 0° C., with a cooling rate of from 1K/s to 30K/s.

18. The method according to claim 1 , wherein a at least one decorative film with a carrier ply made of PET with a thickness of from 5 μm to 250 μm is used.