Metal-assisted etch combined with regularizing etch
In an aspect of the disclosure, a process for forming nanostructuring on a silicon-containing substrate is provided. The process comprises (a) performing metal-assisted chemical etching on the substrate, (b) performing a clean, including partial or total removal of the metal used to assist the chemical etch, and (c) performing an isotropic or substantially isotropic chemical etch subsequently to the metal-assisted chemical etch of step (a). In an alternative aspect of the disclosure, the process comprises (a) performing metal-assisted chemical etching on the substrate, (b) cleaning the substrate, including removal of some or all of the assisting metal, and (c) performing a chemical etch which results in regularized openings in the silicon substrate.
1. A process for forming nanostructuring on a silicon-containing substrate, the process comprising:
(a) performing metal-assisted chemical etching on the substrate to form nanostructured depressions extending downward from a surface of the substrate;
(b) performing a clean subsequently to the metal-assisted chemical etch of step (a), the clean including removal of substantially all of the metal used to assist the chemical etch; and
(c) performing an isotropic or substantially isotropic chemical etch subsequently to the clean of step (b), the isotropic or substantially isotropic chemical etch etching the surface the substrate and bottoms of the depressions at approximately a same rate.
2. The process of claim 1 , wherein the isotropic or substantially isotropic etch of step (c) comprises immersion in an etchant solution comprising HNO 3 and HF.
3. The process of claim 2 , wherein the etchant solution further comprises acetic acid.
4. The process of claim 1 , wherein the etch of step (a) removes between about 0.3 and about 3 times as much material, measured in nm, as the etch of step (c).
5. The process of claim 1 , wherein the step (a) comprises depositing the metal which assists the etch and subjecting the deposited metal to a process of agglomeration.
6. The process of claim 5 , wherein the step (a) comprises etching the agglomerated metal.
7. The process of claim 5 , wherein the process of agglomeration comprises annealing.
8. The process of claim 5 , wherein the process of agglomeration is performed in a liquid solution.
9. The process of claim 1 , wherein the result of (c) is further processed to form an optoelectronic or photovoltaic device with nanostructuring.
10. The process of claim 9 , wherein the device formed is a solar cell.
11. The process of claim 10 , wherein the solar cell formed exceeds the efficiency of a solar cell with otherwise identical processing in which nanostructuring is formed by means of metal-assisted chemical etching not followed by a further isotropic or substantially isotropic chemical etch.
12. The process of claim 10 , wherein the solar cell formed exceeds the efficiency of a solar cell with otherwise identical processing in which nanostructuring is formed by means of reactive ion etching.
13. The process of claim 10 , wherein the solar cell is not subject to a step of removing saw damage.
14. The process of claim 1 , wherein the etching removes material in such a way that the result of step (c) comprises nanowires.
15. The process of claim 1 , wherein the metal-assisted chemical etching of step (a) is an anisotropic etch.
16. A process for forming nanostructuring on a silicon-containing substrate, the process comprising:
(a) performing metal-assisted chemical etching on the substrate to form nanostructured depressions extending downward from a surface of the substrate;
(b) performing a clean of the substrate and nanostructured depressions formed in step (a) subsequently to the metal-assisted chemical etch of step (a) to form a cleaned substrate, the clean including removal of substantially all of the metal used to assist the chemical etch; and
(c) performing an isotropic or substantially isotropic chemical etch of the cleaned substrate formed in act (b) subsequently to the clean of step (b), the isotropic or substantially isotropic chemical etch etching the surface the substrate and bottoms of the depressions at approximately a same rate.
17. The process of claim 16 , wherein the metal-assisted chemical etching of step (a) is an anisotropic etch.