Ternary ceramic thermal spraying powder and method of manufacturing thermal sprayed coating using said powder
The invention describes a method for producing ternary and binary ceramic powders and their thermal spraying capable of manufacturing thermal sprayed coatings with superior properties. Powder contain at least 30% by weight ternary ceramic, at least 20% by weight binary molybdenum borides, at least one of the binary borides of Cr, Fe, Ni, W and Co and a maximum of 10% by weight of nano and submicro-sized boron nitride. The primary crystal phase of the manufactured thermal sprayed coatings from these powders is a ternary ceramic, while the secondary phases are binary ceramics. The coatings have extremely high resistance against corrosion of molten metal, extremely thermal shock resistance and superior tribological properties at low and at high temperatures.
1. A method of forming a thermal sprayed coating on a substrate, the steps comprising:
providing a thermal spray powder comprising:
one or more ternary boride ceramics of Metal-Mo—B, Metal-Mo 2 —B 2 , or Metal 2 -Mo 2 —B 2 from about 20-70% by weight, where Metal is Ni;
one or more binary molybdenum borides from 0-60% by weight; and,
one or more metal binary borides from 0-50% by weight, where the one or more metal binary borides are selected from Cr, Fe, or Ni; and,
thermally spraying the thermal spray powder onto the substrate.
2. The method of forming a thermal sprayed coating of claim 1 , where the thermal spray powder used in the step of spraying is comprised of particle sizes ranging between 5 and 125 μm (micrometers).
3. The method of forming a thermal sprayed coating of claim 1 , where the thermal spray powder used in the step of spraying is comprised of particle sizes ranging between 10 and 45 μm (micrometers).
4. The method of forming a thermal sprayed coating of claim 1 , where the step of thermally spraying is performed by plasma thermal spraying, flame spraying, detonation spraying, cold gas spraying, arc spraying, or high velocity oxygen fuel spraying.
5. The method of forming a thermal sprayed coating of claim 1 , where the thermal spray powder further comprises:
one or more nano and submicro-sized reinforced solid lubricants from 0-10% by weight, the one or more nano and submicrosized reinforced solid lubricants comprising BN, WS 2 or MoS 2 .
6. The method of forming a thermal sprayed coating of claim 1 , where the step of spraying forms a coating on the substrate from the thermal spray powder having a thickness of 50 to 300 μm.
7. The method of forming a thermal sprayed coating of claim 1 , where the substrate is a metal.
8. The method of forming a thermal sprayed coating of claim 1 , where the coating is characterized as having a corrosion resistance coating against molten metal.
9. The method of forming a thermal sprayed coating of claim 1 , where the coating is characterized as having a dense, superfine structured and homogeneous morphology with a porosity less than 1%.
10. The method of forming a thermal sprayed coating of claim 1 , where the coating is characterized as having a Vickers hardness of 895±61 HV0.3.
11. The method of forming a thermal sprayed coating of claim 1 , where the one or more binary molybdenum borides is 20-60% by weight.
12. The method of forming a thermal sprayed coating of claim 1 , where the one or more metal binary borides is 10-50% by weight.