Ultrasound coupling material and method of use
A method of releasably adhering an ultrasonic sensor to a structure, the structure having an operating temperature range, the method comprising: applying a coupling agent between the structure and the sensor at an installation temperature, the coupling agent having a glass transition temperature (Tg) below the operating temperature range and below the installation temperature, the coupling agent being in a viscous/viscoelastic state over the operating temperature range; and urging the sensor against the structure with the coupling agent therebetween such that the sensor adheres to the structure.
1. A method of releasably adhering an ultrasonic sensor to a structure, said structure having an operating temperature range, said method comprising:
applying a coupling agent between said structure and said sensor at an installation temperature, said coupling agent having a glass transition temperature (Tg) below said operating temperature range and below said installation temperature, said coupling agent being in a viscous/viscoelastic state over said operating temperature range; and
urging said sensor against said structure with said coupling agent therebetween such that said sensor adheres to said structure.
2. The method of claim 1 , further comprising:
removing said sensor from said structure by pulling said sensor away from said structure at a temperature below said operating range at which said coupling agent has a surface tension no greater than 40 mN/m.
3. The method of claim 1 , wherein said coupling agent has a surface tension of less than 40 mN/m above said Tg.
4. The method of claim 1 , wherein said Tg is substantially below said operating range.
5. The method of claim 1 , wherein said Tg is at least 50° C. below said operating range.
6. The method of claim 5 , wherein said Tg is less than −20° C.
7. The method of claim 6 , wherein said Tg is less than −60° C.
8. The method of claim 1 , wherein said coupling agent has a melting temperature Tm, and said Tm is greater than said operating range.
9. The method of claim 1 , wherein said coupling agent is a polymer.
10. The method of claim 9 , wherein said polymer is selected from the group consisting of polyalkanedienes, polyalkenes and polysiloxanes.
11. The method of claim 10 , wherein said polymer is selected from the group consisting of polyisoprene, poly(1 butylene), poly(1-pentylene), poly(1-ethyl-1-butylene), poly (1-butyl-1-butylene), poly(1-heptyl-1-butylene), polyisobutene, poly(oxydimethylsilylene)(=polydimethylsiloxane), and poly(oxymethylphenylsilylene).
12. The method of claim 11 , wherein said polymer is selected from the group consisting of polyisobutene and poly(oxydimethylsilylene).
13. The method of claim 12 , wherein said polymer is selected from the group consisting of Stopaq CZ™ paste, Stopaq CZH™ paste, Stopaq CZHT™ paste, and Viscotag™ viscopaste.