Low density foam, midsole, footwear, and methods for making low density foam

1. A method for making a low density foamed article, comprising:

combining in an extruder a molten thermoplastic ethylene-vinyl acetate copolymer with

(a) a chemical blowing agent and

(b) a supercritical fluid,

to form a mixture, wherein the chemical blowing agent (a) is present in an amount up to about 15 weight percent based on total polymer weight in the mixture and the supercritical fluid (b) comprises one of about 0.1 to about 5 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or about 0.1 to about 4 weight percent of supercritical N 2 based on the total polymer weight in the mixture, and

injecting the mixture into a mold at an injection pressure of from 110 megapascal to about 207 megapascal, and molding the mixture to form the low density foamed article, wherein the mold comprises a porous tool;

wherein the low density foamed article has a density of less than 0.3 grams per cubic centimeter.

2. The method according to claim 1 , wherein the molten thermoplastic ethylene-vinyl acetate copolymer comprises from about 25 weight percent to about 50 weight percent vinyl acetate content.

3. The method according to claim 1 , wherein the chemical blowing agent is present in an amount from about 3 to about 12 weight percent based on the total polymer weight in the mixture.

4. The method according to claim 1 , wherein the supercritical fluid is one of from about 0.5 to about 3 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or from about 0.4 to about 2.5 weight percent of supercritical N 2 based on the total polymer weight in the mixture.

5. The method according to claim 1 , wherein the mixture further comprises a crosslinker.

6. The method according to claim 1 , wherein the porous tool has a pore size of from about 3 micrometers to about 20 micrometers.

7. The method according to claim 1 , wherein the porous tool is a porous metal or metal alloy.

8. The method according to claim 1 , wherein the porous tool is an insert having dimensions of the mold cavity.

9. The method according to claim 1 , wherein the porous tool comprises a plurality of inserts spaced within the mold cavity.

10. A method for making a low density foamed article, comprising:

combining in an extruder a molten thermoplastic ethylene-vinyl acetate copolymer having a melt index of from about 0.5 up to about 50 grams/10 minutes at 190° C., 8.7 kg as measured using the procedure of ASTM D1238 with

(a) a chemical blowing agent and

(b) a supercritical fluid

to form a mixture, wherein the chemical blowing agent (a) is present in an amount up to 15 wt % based on total polymer weight in the mixture and the supercritical fluid (b) comprises one of about 0.1 to about 5 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or about 0.1 to about 4 weight percent of supercritical N 2 based on the total polymer weight in the mixture, and

injecting the mixture into a mold at an injection pressure of from 110 megapascal to about 207 megapascal, and molding the mixture to form the low density foamed article.

11. The method according to claim 10 , wherein the molten thermoplastic ethylene-vinyl acetate copolymer comprises from about 25 weight percent to about 50 weight percent vinyl acetate content.

12. The method according to claim 10 , wherein the chemical blowing agent is present in an amount from about 3 to about 12 weight percent based on the total polymer weight in the mixture.

13. The method according to claim 10 , wherein the supercritical fluid is one of from about 0.5 to about 3 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or from about 0.4 to about 2.5 weight percent of supercritical N 2 based on the total polymer weight in the mixture.

14. A method for making a low density foamed article, comprising:

combining in an extruder a molten thermoplastic ethylene-vinyl acetate copolymer having a melt index of from about 0.5 up to about 50 grams/10 minutes at 190° C., 8.7 kg as measured using the procedure of ASTM D1238 with

(a) a chemical blowing agent and

(b) a supercritical fluid

to form a mixture, wherein the chemical blowing agent is present in an amount up to 15 wt % based on total polymer weight in the mixture and the supercritical fluid comprises one of about 0.1 to about 5 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or about 0.1 to about 4 weight percent of supercritical N 2 based on the total polymer weight in the mixture, and

injecting the mixture into a mold at an injection pressure of from 110 megapascal to about 207 megapascal, and molding the mixture to form the low density foamed article; wherein the mold comprises a porous tool;

wherein the low density foamed article has a density of less than 0.3 grams per cubic centimeter.

15. The method according to claim 14 , wherein the chemical blowing agent is present in an amount from about 3 to about 12 weight percent based on the total polymer weight.

16. The method according to claim 14 , wherein the supercritical fluid is one of from about 1 to about 3 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or from about 0.4 to about 2.5 weight percent of supercritical N 2 based on the total polymer.

17. A low density foamed article made by the method of claim 1 .

18. The low density foamed article according to claim 17 , wherein the article has a density of from about 0.15 to less than 0.3 grams per cubic centimeter.

19. The low density foamed article according to claim 17 , wherein the article is a cushion or cushioning element for an article of footwear, protective equipment, or clothing.