Leakage control for gate-all-around field-effect transistor devices
Techniques are provided to fabricate embedded insulating layers within an active semiconductor layer of substrate to reduce leakage between field-effect transistor devices and the semiconductor substrate. For example, an epitaxial semiconductor layer is formed on a surface of a semiconductor substrate. An ion implantation process is performed to form an embedded insulation layer within the semiconductor substrate below the epitaxial semiconductor layer. A nanosheet field-effect transistor device is formed over the embedded insulation layer. The nanosheet field-effect transistor device includes active nanosheet channel layers, source/drain layers, and a high-k dielectric/metal gate structure formed around the active nanosheet channel layers. The process of forming the nanosheet field-effect transistor device includes removing the epitaxial semiconductor layer to release the active nanosheet channel layers. The embedded insulation layer isolates the high-k dielectric/metal gate structure and the source/drain layers from the semiconductor substrate.
1. A method for fabricating a semiconductor device, comprising:
forming a first epitaxial semiconductor layer on a surface of a semiconductor substrate;
forming a screening layer over the first epitaxial semiconductor layer;
performing an ion implantation process to form an embedded insulation layer within the semiconductor substrate below the first epitaxial semiconductor layer;
forming a nanosheet field-effect transistor device over the embedded insulation layer, wherein the nanosheet field-effect transistor device comprises a plurality of active nanosheet channel layers, source/drain layers in contact with end portions of the active nanosheet channel layers, and a high-k dielectric/metal gate structure formed around the active nanosheet channel layers;
wherein forming the nanosheet field-effect transistor device comprises removing the first epitaxial semiconductor layer to release the active nanosheet channel layers;
wherein the embedded insulation layer isolates the high-k dielectric/metal gate structure and the source/drain layers from the semiconductor substrate;
wherein the screening layer is formed over the first epitaxial semiconductor layer, prior to performing the oxygen ion implantation process; and
wherein performing the ion implantation process to form the embedded insulation layer within the semiconductor substrate below the first epitaxial semiconductor layer comprises:
performing an oxygen ion implantation process to form an oxygen ion implant region within an upper surface region of the semiconductor substrate below the first epitaxial semiconductor layer; and
performing a thermal anneal process to convert the oxygen ion implant region to an embedded oxide layer.
2. The method of claim 1 , wherein parameters of the oxygen ion implantation process are configured to form the oxygen ion implant region having an oxygen ion concentration of about 1×10 16 atoms/cm 3 to about 1×10 22 atoms/cm 3 .
3. The method of claim 1 , wherein the semiconductor substrate comprises a silicon substrate and wherein the embedded oxide layer comprises a silicon oxide layer.
4. The method of claim 1 , wherein the embedded oxide layer has a thickness in a range of about 5 nm to about 100 nm.
5. The method of claim 1 , wherein the screening layer comprises a screening oxide layer formed over the first epitaxial semiconductor layer.
6. The method of claim 5 , wherein the screening layer further comprises a screening nitride layer formed over the screening oxide layer.
7. A method for fabricating a semiconductor device, comprising:
forming a first epitaxial semiconductor layer on a surface of a semiconductor substrate;
performing an ion implantation process to form an embedded insulation layer within the semiconductor substrate below the first epitaxial semiconductor layer;
forming a nanosheet field-effect transistor device over the embedded insulation layer, wherein the nanosheet field-effect transistor device comprises a plurality of active nanosheet channel layers, source/drain layers in contact with end portions of the active nanosheet channel layers, and a high-k dielectric/metal gate structure formed around the active nanosheet channel layers;
wherein the embedded insulation layer isolates the high-k dielectric/metal gate structure and the source/drain layers from the semiconductor substrate; and
wherein forming the nanosheet field-effect transistor device over the embedded insulation layer comprises:
forming a nanosheet layer stack over the embedded insulation layer, wherein the nanosheet layer stack comprises a plurality of epitaxial semiconductor layers comprising sacrificial nanosheet layers and the active nanosheet channel layers, wherein the first epitaxial semiconductor layer comprises a sacrificial nanosheet layer of the nanosheet layer stack;
patterning the nanosheet layer stack down to the embedded insulation layer to thereby form a nanosheet stack structure which is disposed on the embedded insulation layer;
forming source/drain layers in contact with exposed sidewall surfaces of the active nanosheet channel layers of the nanosheet stack structure;
selectively etching the first epitaxial semiconductor layer and the sacrificial nanosheet layers of the nanosheet stack structure to remove the first epitaxial semiconductor layer and the sacrificial nanosheet layers and thereby release the active nanosheet channel layers; and
forming the high-k dielectric/metal gate structure which surrounds the active nanosheet channel layers.
8. The method of claim 7 , wherein the first epitaxial semiconductor layer and the sacrificial nanosheet layers are formed of epitaxial silicon germanium, and wherein the active nanosheet layers are formed of epitaxial silicon.
9. A method for fabricating a semiconductor device, comprising:
forming a first epitaxial semiconductor layer on active silicon layer of a semiconductor substrate;
forming a screening layer over the first epitaxial semiconductor layer;
performing an oxygen ion implantation process to form an embedded oxide layer within the active silicon layer below the first epitaxial semiconductor layer;
performing an etch process to remove the screening layer selective to the first epitaxial semiconductor layer;
forming a nanosheet layer stack over the embedded insulation layer, wherein the nanosheet layer stack comprises a plurality of epitaxial semiconductor layers comprising sacrificial nanosheet layers and active nanosheet channel layers, wherein the first epitaxial semiconductor layer comprises a sacrificial nanosheet layer of the nanosheet layer stack;
patterning the nanosheet layer stack down to the embedded oxide layer to thereby form a nanosheet stack structure which is disposed on the embedded oxide layer;
forming source/drain layers in contact with exposed sidewall surfaces of the active nanosheet channel layers of the nanosheet stack structure;
selectively etching the sacrificial nanosheet layers of the nanosheet stack structure to release the active nanosheet channel layers; and
forming a high-k dielectric/metal gate structure which surrounds the active nanosheet channel layers;
wherein the embedded oxide layer isolates the high-k dielectric/metal gate structure and the source/drain layers from the semiconductor substrate.
10. The method of claim 9 , wherein performing the oxygen ion implantation process to form the embedded oxide layer within the active silicon layer below the first epitaxial semiconductor layer comprises:
performing an oxygen ion implantation process to form an oxygen ion implant region within an upper surface region of the active silicon layer of the semiconductor substrate below the first epitaxial semiconductor layer; and
performing a thermal anneal process to convert the oxygen ion implant region to an embedded silicon dioxide layer.
11. The method of claim 10 , wherein parameters of the oxygen ion implantation process are configured to form the oxygen ion implant region having an oxygen ion concentration of about 1×10 16 atoms/cm 3 to about 1×10 22 atoms/cm 3 .
12. The method of claim 10 , wherein the embedded silicon dioxide layer has a thickness in a range of about 5 nm to about 100 nm.
13. The method of claim 9 , wherein the screening layer comprises a screening oxide layer formed over the first epitaxial semiconductor layer.
14. The method of claim 13 , wherein the screening layer further comprises a screening nitride layer formed over the screening oxide layer.
15. The method of claim 9 , wherein the sacrificial nanosheet layers are formed of epitaxial silicon germanium, and wherein the active nanosheet layers are formed of epitaxial silicon.
16. The method of claim 1 , further comprising performing an etch process to remove the screening layer selective to the first epitaxial semiconductor layer, prior to forming the nanosheet field-effect transistor device.
17. The method of claim 7 , wherein performing the ion implantation process to form the embedded insulation layer within the semiconductor substrate below the first epitaxial semiconductor layer, comprises:
performing an oxygen ion implantation process to form an oxygen ion implant region within an upper surface region of the semiconductor substrate below the first epitaxial semiconductor layer; and
performing a thermal anneal process to convert the oxygen ion implant region to an embedded oxide layer;
wherein parameters of the oxygen ion implantation process are configured to form the oxygen ion implant region having an oxygen ion concentration of about 1×10 16 atoms/cm 3 to about 1×10 22 atoms/cm 3 .
18. The method of claim 17 , wherein the semiconductor substrate comprises a silicon substrate and wherein the embedded oxide layer comprises a silicon oxide layer.
19. The method of claim 17 , wherein the embedded oxide layer has a thickness in a range of about 5 nm to about 100 nm.