Exemplary FET devices having 2D material layer active regions and methods of fabricating thereof are described. For example, a black phosphorus active region has a first thickness in the channel region and a second, greater, thickness in the source/drain (S/D) region. The BP in the S/D region has a sidewall that interfaces a contact disposed over the FET. A gate electrode is disposed over the channel region. In some embodiments, the sidewall has passivated edge. In some embodiments, the sidewall is nonlinear. In some embodiments, the stress layer is disposed over the 2D material layer.
1. A method of forming a field-effect transistor (FET), comprising:
forming a 2D material layer having a first thickness over a substrate, the 2D material layer including a channel region and a source/drain region;
etching the 2D material layer in the channel region to form the 2D material layer in the channel region having a second thickness, the second thickness being less than the first thickness;
forming a gate structure over the channel region having the second thickness;
forming a dielectric layer over the source/drain region of the 2D material layer; and
forming a hole in the dielectric layer and exposing the 2D material layer.
2. The method of claim 1 , wherein the forming the 2D material layer having the first thickness includes forming three monolayers of phosphorene.
3. The method of claim 2 , wherein the etching the 2D material layer removes at least one monolayer of the three monolayers of phosphorene.
4. The method of claim 1 , filling the hole with conductive material to form a contact.
5. The method of claim 4 , wherein the conductive material interfaces a sidewall of the 2D material layer.
6. The method of claim 5 , wherein the conductive material interface with the sidewall of the 2D material layer extends the second thickness.
7. The method of claim 1 , wherein the forming the hole exposing the 2D material layer removes at least one monolayer of the 2D material layer to form the 2D material layer of a third thickness, the third thickness less than the second thickness.
8. The method of claim 1 , further comprising:
a passivating an edge of the 2D material layer.
9. The method of claim 1 , further comprising:
providing the substrate, wherein the substrate has a plurality of fins extending from the substrate, wherein the forming the 2D material layer having the first thickness over the plurality of fins.
10. A method of forming a device, the method comprising:
forming a black phosphorous (BP) layer on a dielectric layer, wherein the BP layer is a first thickness;
reducing the first thickness of the BP layer in a first region to a second thickness, while maintaining the first thickness in a second region;
forming a gate structure over the first region of the BP layer; and
forming a contact interfacing the BP layer over the second region.
11. The method of forming the device of claim 10 , wherein the forming the contact includes reducing the first thickness to a third thickness.
12. The method of claim 11 , wherein the forming the contact forms a conductive material interfacing the BP layer of the third thickness.
13. The method of claim 11 , wherein a difference between the first thickness and the second thickness is 2 monolayers and wherein a difference between the first thickness and the third thickness is 1 monolayer.
14. The method of claim 10 , further comprising: doping an edge of the BP layer with at least one of selenium or sulfur.
15. The method of claim 10 , wherein the forming the gate structure includes depositing a gate dielectric layer of the gate structure interfacing the BP layer having the second thickness.
16. The method of claim 10 , wherein the reducing the first thickness includes etching a monolayer of the BP layer.
17. A method of fabricating a field effect transistor (FET), comprising:
forming a black phosphorous (BP) layer on a substrate, wherein the BP layer has a first edge and a second edge transverse to the first edge;
removing at least one layer of the BP layer in a channel region;
forming a gate structure over the channel region;
passivating the first edge; and
forming a contact interfacing the passivated first edge.
18. The method of claim 17 , wherein the passivating includes doping the BL layer.
19. The method of claim 18 , wherein the doping the BL layer includes exposing the BP layer to a mixture of oxygen, sulfur and selenium.
20. The method of claim 17 , wherein the forming the BP layer includes forming the first edge being non-linear.