Coating composition and coated paper and coated paperboard
A coating composition may include kaolin having a shape factor less than about 70 and calcium carbonate, wherein less than about 90% by weight and greater than about 60% by weight of particles of the calcium carbonate have an equivalent spherical diameter (esd) less than 2 microns. The coating composition may include a thickener present in an amount ranging from about 0.1% to about 0.9% by active dry weight of the composition. A coating composition may include kaolin having a shape factor less than about 70 and calcium carbonate having a mean particle size (d50) of at least about 2.4 microns and a steepness factor of at least about 30. The coating composition may be a paper basecoat composition or a paperboard basecoat composition. A paper or paperboard product may include the coating composition on at least one surface of the paper product or paperboard product.
1. A coating composition comprising:
kaolin having a shape factor less than about 70; and
calcium carbonate having a d 50 of at least about 2.4 microns, wherein less than 70% by weight and greater than 60% by weight of particles of the calcium carbonate have an equivalent spherical diameter less than 2 microns.
2. The coating composition of claim 1 , further comprising a thickener.
3. The coating composition of claim 2 , wherein the thickener is present in an amount ranging from about 0.1% to about 0.9% by active dry weight of the coating composition.
4. The coating composition of claim 2 , wherein the thickener is selected from the group consisting of alkali-soluble emulsion polyacrylate thickeners, hydrophobically-modified alkali-soluble emulsion polyacrylate thickeners, and carboxymethyl cellulose thickeners.
5. The coating composition of claim 1 , wherein less than about 30% by weight of the kaolin has an equivalent spherical diameter less than about 0.25 microns.
6. The coating composition of claim 1 , wherein the calcium carbonate has a d 50 of at least about 2.6 microns.
7. The coating composition of claim 1 , wherein the calcium carbonate has a steepness factor greater than 32.
8. The coating composition of claim 1 , further comprising a binder, wherein the binder comprises at least one of an adhesive binder, a starch binder, a synthetic binder, a polyvinyl acetate-based binder, or an acrylic binder.
9. The coating composition of claim 8 , wherein the binder forms from 4% to 30% by weight of a solids content of the coating composition.
10. A paperboard product comprising the coating composition of claim 1 on at least one surface of the paperboard product, wherein the paperboard product has a total weight per unit area ranging from 30 g/m 2 to 70 g/m 2 .
11. A method of reducing the cracking and/or flaking of a coated paperboard product at a fold, the method comprising:
i) providing a coating composition on a paperboard product, wherein the coating composition comprises a mixture of a binder, kaolin having a shape factor greater than 50 and less than 70; and
calcium carbonate, wherein less than 70% by weight and greater than about 60% by weight of the particles of the calcium carbonate have an equivalent spherical diameter less than 2 microns; and
ii) folding the paperboard product to form a fold, wherein the paperboard product has a higher modulus and a higher stiffness as compared to a second modulus and a second stiffness of a paperboard product coated with a coating composition devoid of the kaolin and the calcium carbonate.
12. The method of claim 11 , wherein the coating composition further comprises a thickener in an amount ranging from about 0.1% to about 0.9% by active dry weight of the coating composition.
13. The method of claim 12 , wherein the thickener is selected from the group consisting of alkali-soluble emulsion polyacrylate thickeners, hydrophobically-modified alkali-soluble emulsion polyacrylate thickeners, and carboxymethyl cellulose thickeners.
14. The method of claim 11 , wherein less than 30% by weight of the kaolin has an equivalent spherical diameter less than about 0.25 microns.
15. The method of claim 11 , wherein less than 80% by weight of the kaolin has an equivalent spherical diameter less than about 1 microns.
16. The method of claim 11 , wherein less than 70% by weight and greater than 60% by weight of the particles of the calcium carbonate have an equivalent spherical diameter less than 2 microns.
17. The method of claim 11 , wherein the binder comprises at least one of an adhesive binder, a starch binder, a synthetic binder, a polyvinyl acetate-based binder, or an acrylic binder.
18. The method of claim 11 , wherein the binder forms from 4% to 30% by weight of a solids content of the coating composition.