Quantum dot surface ligand exchange method
Provided is a quantum dot surface ligand exchange method. The method comprises the steps: pre-treating proton-containing ligands using a deprotonating agent to obtain deprotonated ligands; mixing a pre-prepared quantum dot solution having original ligands with the deprotonated ligands, after stirring for a predetermined amount of time at room temperature, a ligand exchange reaction occurring, and after washing, obtaining a quantum dot having the deprotonated ligands on the surface. The quantum dot ligand exchange method has a high reaction rate and is easy to operate; after the ligand exchange, the deprotonated ligands firmly bind to cations on the surface of the quantum dot, and after the ligand exchange, the quantum dot provides a stable colloidal solution, and has good solubility and high luminous efficiency.
1. A quantum dot surface ligand exchange method, comprising:
pretreating a proton-containing ligand by a deprotonating agent, and obtaining a deprotonated ligand, wherein the proton-containing ligand is a proton-containing amine, and the deprotonating agent is an acyl chloride or sulfonyl chloride;
mixing a solution of a quantum dot having an original ligand with the deprotonated ligand for a ligand exchange reaction to occur;
completing the ligand exchange reaction; and
obtaining a quantum dot having a surface of the deprotonated ligand.
2. The quantum dot surface ligand exchange method according to claim 1 , further comprising: adding the deprotonating agent to a solution of the proton-containing ligand, stirring at a room temperature for 15-120 min, before obtaining the deprotonated ligand.
3. The quantum dot surface ligand exchange method according to claim 2 , wherein, the deprotonating agent is added to the solution of the proton-containing ligand at a molar ratio 1:1-6 of the deprotonating agent to the proton-containing ligand.
4. The quantum dot surface ligand exchange method according to claim 1 , further comprising: after the ligand exchange reaction has completed, standing for 10-30 min, finally adding ethyl acetate and centrifugating for 2-4 times, before obtaining the quantum dot having the surface of the deprotonated ligand.
5. The quantum dot surface ligand exchange method according to claim 1 , wherein in the solution of the quantum dot having the original ligand, the original ligand of the quantum dot is one of a trioctylphosphine, a trioctylphosphine oxide, a tributylphosphine, a tributylphosphine oxide, an oleic acid, a stearic acid, and an oleylamine.
6. The quantum dot surface ligand exchange method according to claim 1 , wherein, the solution of the quantum dot having the original ligand is mixed with the deprotonated ligand at a molar ratio 1:1-8 of the quantum dot having the original ligand to the deprotonated ligand.
7. The quantum dot surface ligand exchange method according to claim 1 , wherein, the proton-containing amine is one of an alkylamine, a mercaptoamine, an amino acid or an amide.
8. The quantum dot surface ligand exchange method according to claim 1 , wherein the proton-containing amine is a water soluble ligand, the step of pretreating the proton-containing ligand by the deprotonating agent, and obtaining the deprotonated ligand comprises: using the deprotonating agent to pretreat a solution of the water soluble ligand, before obtaining a water soluble deprotonated ligand.
9. The quantum dot surface ligand exchange method according to claim 1 , wherein the proton-containing amine is an oil soluble ligand, and pretreating the proton-containing ligand by the deprotonating agent, and obtaining the deprotonated ligand comprises:
using the deprotonating agent to pretreat a solution of the oil soluble ligand, to form a phase separated solution including an aqueous phase and a solution phase;
removing the aqueous phase; and
obtaining a solution containing an oil soluble deprotonated ligand.
10. The quantum dot surface ligand exchange method according to claim 1 , wherein a material of the quantum dot is selected from at least one of: CdSe, CdS, ZnSe, ZnS, PbSe, PbS, CdTe, Cd 1-x Zn x S, Cd 1-x Zn x Se, CdSe y S 1-y , Cd 1-x Zn x Se y S 1-y , PbSe x S 1-x , Zn x Cd 1-x Te, CdSe/ZnS, CdS/ZnS, Cd 1-x Zn x Se/ZnS, Cd 1-x Zn x S/ZnS, CdSe/CdS/ZnS, CdSe/ZnSe/ZnS, CdS/Cd 1-x Zn x S/Cd y Zn 1-y S/ZnS, CdSe/Cd 1-x Zn x Se/CdyZn 1-y Se/ZnSe, InP, InP/ZnS, ZnO, MgO, CeO 2 , NiO, TiO 2 , CaF 2 , NaYF 4 , and NaCdF 4 .