Dielectric filter and method for manufacturing the same
The invention relates to a method of manufacturing a dielectric filter. The method comprises the steps of: (a) preparing a ceramic substrate; (b) applying a conductive paste on the ceramic substrate, wherein the conductive paste comprises, (i) 100 parts by weight of a conductive powder, (ii) 0.1 to 10.0 parts by weight of a glass frit comprising silicon oxide, boron oxide, aluminum oxide and an alkaline metal oxide, and (iii) an organic vehicle; and (c) firing the applied conductive paste.
1. A method of manufacturing a dielectric filter, comprising the steps of:
(a) preparing a ceramic substrate having a dielectric constant, εy, of 9 to 50 that does not include Aluminum Nitride (AlN);
(b) applying a conductive paste on the ceramic substrate, wherein the conductive paste comprises,
(i) 100 parts by weight of a conductive powder,
(ii) 0.1 to 10.0 parts by weight of a glass frit comprising 30 to 85 wt. % of silicon oxide, 11 to 50 wt. % of boron oxide and 0.1 to 5.0 wt. % of aluminum oxide and 0.5 to 6 wt. % of an alkali metal oxide based on the weight of the glass frit, and
(iii) an organic vehicle; and
(c) firing the applied conductive paste.
2. The method of claim 1 , wherein the glass frit further comprises an additional metal oxide selected from the group consisting of zirconium oxide, titanium oxide, calcium oxide, zinc oxide, magnesium oxide, copper oxide, iron oxide and a combination thereof.
3. The method of claim 2 , wherein the additional metal oxide is selected from the group consisting of zirconium oxide, titanium oxide, zinc oxide, copper oxide, iron oxide and a combination thereof.
4. The method of claim 2 , wherein the additional metal oxide is 0.5 to 20 wt. % based on the weight of the glass frit.
5. The method of claim 1 , wherein at least 60 mol % of metal components of the ceramic substrate are selected from the group consisting of Al, Ba, Ca, La, Mg, Mn, Nb, Nd, Ni, Pb, Sm, Sn, Sr, Ta, Ti, Zn, Zr and a mixture thereof.
6. The method of claim 1 , wherein the conductive paste is applied on the entire surface of the ceramic substrate.
7. The method of claim 1 , wherein the dielectric filter operates in a TEM (transverse electromagnetic) mode.
8. The method of claim 1 , wherein a particle diameter (D 50 ) of the conductive powder is 0.01 to 10 μm.
9. The method of claim 1 , wherein the alkali metal oxide comprises lithium oxide, sodium oxide and potassium oxide.
10. The method of claim 1 , wherein the firing temperature in step (c) is 600 to 1100° C.