US 12,391,595 · App. 16/938,074 · Granted Aug 19, 2025

Inventors: Alexander Glacki (Mainz, DE); Christian Breitbach (Darmstadt, DE); Holger Hunnius (Mainz, DE); Ulrich Lange (Mainz, DE); Wolfgang Munch (Budenheim, DE); Gregor Rösel (Ginsheim-Gustavsburg, DE); Volker Seibert (Hochheim, DE); Holger Wegener (Alfeld, DE)

Assignee: SCHOTT AG

C03B17/062C03B17/068

Abstract

Claims (75)

1. A method for producing a glass ribbon, comprising:

suspending a guiding body via a mount so that the guiding body is self-supporting at least along a section of a nozzle opening over which a central area of the glass ribbon is formed, the central area having a uniform thickness that is less than a thickness of two edge-side beads of the glass ribbon,

wherein the guiding body is at least partially mounted inside a drawing tank,

wherein the guiding body comprises a resistance body arranged inside the drawing tank and a blade arranged below the resistance body, wherein the resistance body has a width that is greater than a width of the blade,

wherein the drawing tank has portions that define the nozzle opening, and

wherein the mount of the guiding body is located above the nozzle opening and the portions are removable while the guiding body remains on the mount;

feeding a molten glass to the drawing tank;

causing the molten glass to exit the drawing tank from the nozzle opening of the drawing tank in two substreams so that the molten glass runs along a portion of the guiding body protruding out of the nozzle opening;

combining the two substreams at a lower end of the guiding body to form a drawing onion;

drawing the glass ribbon off the drawing onion, wherein the step of drawing of the glass ribbon exerts a tensile force on the guiding body; and

absorbing the tensile force with the mount of the guiding body.

2. The method of claim 1 , wherein the step of drawing the glass ribbon further comprises controlling a temperature of the molten glass to a forming temperature of more than 1100° C.

3. The method of claim 1 , further comprising supplying electric current through the mounts to directly conductively heat the guiding body.

4. The method of claim 1 , wherein the tensile force is absorbed at lateral ends of the guiding body.

5. A method for producing a glass ribbon, comprising:

feeding a molten glass to a drawing tank;

adjusting a temperature of the molten glass in the drawing tank so that for a temperature-dependent viscosity n thereof the following relationship applies:

48

⁢

v

.

B

⁢

∫

H

L

⁢

η

(

D

S

-

D

L

)

3

⁢

d

⁢

z

+

1

⁢

2

⁢

v

.

B

⁢

∫

H

S

⁢

η

D

S

3

⁢

d

⁢

z

>

ρ

·

g

·

h

-

p

u

wherein {dot over (v)} is a volume flow of the molten glass, B is a width of the drawing tank in a direction along the nozzle opening, D S is a local width of the drawing tank, D L is a local thickness of the guiding body, ρ is a density of the molten glass, g is a gravitational acceleration, h is a height of the drawing tank, and p u is a pressure of 2000 Pa;

causing the molten glass to exit the drawing tank from a lower nozzle opening of the drawing tank in two substreams so that the molten glass runs along a portion of a guiding body protruding out of the lower nozzle opening;

combining the two substreams at a lower end of the guiding body to form a drawing onion;

drawing the glass ribbon off the drawing onion, wherein the step of drawing of the glass ribbon exerts a tensile force on the guiding body; and

absorbing the tensile force with a mount of the guiding body.