Removal of surface passivation
Methods for removing a passivation film from a copper surface can include exposing the passivation film to a vapor phase organic reactant, for example at a temperature of 100° C. to 400° C. In some embodiments, the passivation film may have been formed by exposure of the copper surface to benzotriazole, such as can occur during a chemical mechanical planarization process. The methods can be performed as part of a process for integrated circuit fabrication. A second material can be selectively deposited on the cleaned copper surface relative to another surface of the substrate.
1. A method of removing copper-containing particles from a dielectric substrate surface comprising copper-containing particles, the method comprising:
contacting the dielectric substrate surface comprising copper-containing particles with a plurality of pulses of a vapor phase organic reactant at a pressure of 0.1 to 50 Torr without exposing the substrate to a plasma, wherein the vapor phase organic reactant interacts with the copper-containing particles to reduce a size of the copper-containing particles and form one or more volatile byproducts, and
removing volatile byproducts from the dielectric substrate surface.
2. The method of claim 1 , wherein the substrate comprises a copper surface that has been subject to chemical mechanical polishing prior to contacting the dielectric substrate surface with the vapor phase organic reactant.
3. The method of claim 2 , wherein the chemical mechanical polishing comprises exposing the copper surface to benzotriazole.
4. The method of claim 1 , wherein volatile byproducts are removed from the dielectric surface by purging with an inert gas.
5. The method of claim 1 , wherein more than 70% of the copper-containing particles that were present on the dielectric substrate surface are removed from the dielectric substrate surface when the dielectric substrate surface comprising copper-containing particles is contacted with the plurality of pulses of the vapor phase organic reactant.
6. The method of claim 1 , wherein the vapor phase organic reactant is an alcohol, an aldehyde, or has the formula R—COOH, where R is hydrogen or a C1 to C3 alkyl.
7. The method of claim 1 , wherein the vapor phase organic reactant comprises a carboxylic acid.
8. The method of claim 1 , wherein the vapor phase organic reactant comprises formic acid.
9. The method of claim 1 , wherein the dielectric substrate surface is contacted with the vapor phase organic reactant at a temperature of 100° C. to 400° C.
10. The method of claim 1 , wherein the copper-containing particles have a longest dimension of up to 20 nm.
11. The method of claim 1 , wherein the copper-containing particles form a passivation layer on the dielectric substrate surface prior to contacting the dielectric substrate surface with the vapor-phase organic reactant.
12. A method for removing at least a portion of a passivation film comprising copper-containing particles from a dielectric substrate surface, the method comprising:
exposing the passivation film to a plurality of pulses of a vapor phase organic reactant comprising an alcohol, an aldehyde or having the formula R—COOH, where R is hydrogen or a C1 to C3 alkyl at a pressure of 0.1 Torr to 50 Torr,
wherein the passivation film was formed on the dielectric substrate surface by subjecting a copper surface on the substrate to chemical mechanical polishing,
wherein the passivation film is not exposed to a plasma during exposure of the passivation film to the vapor phase organic reactant, and
wherein the vapor phase organic reactant interacts with the copper-containing particles to reduce a size of the copper-containing particles and form volatile reaction byproducts; and
removing volatile reaction byproducts from the dielectric substrate surface.
13. The method of claim 12 , wherein the passivation film is exposed to the vapor phase organic reactant at a temperature of 100° C. to 400° C.
14. The method of claim 12 , wherein the vapor phase organic reactant comprises carboxylic acid.
15. The method of claim 12 , wherein the vapor phase organic reactant comprises formic acid.
16. The method of claim 12 , wherein the passivation film is exposed to the vapor phase organic reactant in a plurality of cycles.
17. The method of claim 16 , wherein the passivation film is exposed to the vapor phase organic reactant at least 10 times.
18. The method of claim 12 , wherein removing comprises purging with an inert gas.
19. The method of claim 12 , wherein the copper-containing particles have a longest dimension of up to 20 nm.
20. The method of claim 12 , wherein chemical mechanical polishing comprises exposing the copper surface to benzotriazole.