Optical fiber
An optical fiber comprises a glass fiber comprising a core and a cladding, a primary resin layer being in contact with the glass fiber and covering the glass fiber, and a secondary resin layer covering the primary resin layer, wherein the Young's modulus of the primary resin layer is 0.04 MPa or more and 1.0 MPa or less at 23° C.±2° C., the secondary resin layer consists of a cured product of a resin composition comprising a base resin containing a urethane (meth)acrylate oligomer, a monomer, and a photopolymerization initiator and hydrophobic inorganic oxide particles, and the content of the inorganic oxide particles is 1% by mass or more and 60% by mass or less based on the total amount of the resin composition.
1. An optical fiber comprising a glass fiber comprising a core and a cladding; a primary resin layer being in contact with the glass fiber and covering the glass fiber; and a secondary resin layer covering the primary resin layer,
wherein a Young's modulus of the primary resin layer is 0.04 MPa or more and 1.0 MPa or less at 23° C.±2° C., and
wherein the secondary resin layer consists of a cured product of a resin composition comprising a base resin containing a urethane (meth)acrylate oligomer, a monomer, and a photopolymerization initiator; and hydrophobic inorganic oxide particles, and a content of the inorganic oxide particles is 8% by mass or more and 60% by mass or less based on a total amount of the resin composition.
2. The optical fiber according to claim 1 , wherein the inorganic oxide particle is at least one selected from the group consisting of silicon dioxide, zirconium dioxide, aluminum oxide, magnesium oxide, titanium oxide, tin oxide, and zinc oxide.
3. The optical fiber according to claim 1 , wherein an average primary particle size of the inorganic oxide particles is 500 nm or less.
4. The optical fiber according to claim 1 , wherein a Young's modulus of the secondary resin layer is 1300 MPa or more and 2700 MPa or less at 23° C.±2° C.
5. The optical fiber according to claim 1 , wherein a glass transition temperature of the secondary resin layer is 60° C. or more and 120° C. or less.
6. The optical fiber according to claim 1 , wherein the resin composition contains 18% by mass or more and 50% by mass or less of the monomer based on a total amount of the base resin.
7. The optical fiber according to claim 2 , wherein an average primary particle size of the inorganic oxide particles is 500 nm or less.