Resin composition, optical fiber, and method for producing optical fiber using polyol between 8000 and 20000 average molecular weight
A resin composition for the secondary coating of an optical fiber is a resin composition containing a non-reactive urethane compound having a number average molecular weight of 10000 or more and 50000 or less, a photopolymerizable compound, and a photopolymerization initiator, the content of the non-reactive urethane compound is 0.05 parts by mass or more and 5 parts by mass or less based on the total amount of the resin composition, and the non-reactive urethane compound is a reaction product of a polyol having a number average molecular weight of 8000 or more and 20000 or less, a diisocyanate, and a compound having active hydrogen.
1. A resin composition for secondary coating of an optical fiber, the resin composition comprising:
a non-reactive urethane compound having a number average molecular weight of 10000 or more and 50000 or less;
a photopolymerizable compound; and
a photopolymerization initiator,
wherein a content of the non-reactive urethane compound is 0.05 parts by mass or more and 5 parts by mass or less based on a total amount of the resin composition, and
the non-reactive urethane compound is a reaction product of a polyol having a number average molecular weight of 8000 or more and 20000 or less, a diisocyanate, and a compound having active hydrogen.
2. The resin composition according to claim 1 , wherein the polyol is a polypropylene polyol.
3. The resin composition according to claim 1 , wherein the compound having active hydrogen is a monohydric alcohol.
4. The resin composition according to claim 1 , wherein
the photopolymerizable compound contains 5 parts by mass or more and 40 parts by mass or less of a urethane (meth)acrylate having a number average molecular weight of 500 or more and 6000 or less based on a total amount of the resin composition, and
the urethane (meth)acrylate is a reaction product of a polyol having a number average molecular weight of 300 or more and 2500 or less, a diisocyanate, and a hydroxyl group-containing (meth)acrylate.
5. The resin composition according to claim 1 , wherein the photopolymerizable compound contains 30 parts by mass or more and 70 parts by mass or less of a bisphenol skeleton-containing (meth)acrylate based on a total amount of the resin composition.
6. An optical fiber comprising:
a glass fiber comprising a core and a cladding;
a primary resin layer coating the glass fiber in contact with the glass fiber; and
a secondary resin layer coating the primary resin layer,
wherein the secondary resin layer comprises a cured product of the resin composition according to claim 1 .
7. A method for producing an optical fiber, the method comprising:
an application step of applying the resin composition according to claim 1 to a periphery of a glass fiber comprising a core and a cladding; and
a curing step of curing the resin composition by irradiation with ultraviolet rays after the application step.