Lightweight, reduced density fire rated gypsum panels
A reduced weight, reduced density gypsum panel that includes high expansion vermiculite with fire resistance capabilities that are at least comparable to (if not better than) commercial fire rated gypsum panels with a much greater gypsum content, weight and density.
1. A gypsum core disposed between cover sheets comprising:
a crystalline matrix of set gypsum and high expansion particles, at least 50% of the high expansion particles having an average diameter greater than about 300 micrometers;
the high expansion particles in an amount and distribution in the core effective to provide a High Temperature Shrinkage (S) in the X-Y direction of about 10% or less; and
the gypsum core, when disposed between cover sheets in a panel, effective to provide the panel with a density (D) of about 40 pounds per cubic foot (640 kg/m 3 ) or less and a core hardness of at least about 11 pounds (50 N).
2. The gypsum core according to claim 1 , wherein at least about 50% of the high expansion particles are greater than about 500 micrometers.
3. The gypsum core of claim 1 , the high expansion particles in an amount and distribution in the core effective to provide a Thermal Insulation Index (TI) of about 20 minutes or greater.
4. A gypsum core disposed between cover sheets comprising:
a crystalline matrix of set gypsum and high expansion particles, at least 50% of the high expansion particles having an average diameter greater than about 300 micrometers;
the high expansion particles in an amount and distribution in the core effective to provide a ratio of High Temperature Thickness Expansion (TE) to S (TE/S) of about 0.2 or more; and
the gypsum core, when disposed between cover sheets in a panel, effective to provide the panel with a density (D) of about 40 pounds per cubic foot (640 kg/m 3 ) or less and a core hardness of at least about 11 pounds (50 N).
5. The gypsum core according to claim 4 , wherein at least about 50% of the high expansion particles are greater than about 500 micrometers.
6. The gypsum core according to claim 5 , wherein the ratio of High Temperature Thickness Expansion to Shrinkage (TE/S) is at least about −0.85.
7. The gypsum core according to claim 5 , wherein between about 55% and about 95% of the high expansion particles are greater than about 500 micrometers.
8. The gypsum core according to claim 5 , wherein between about 55% and about 75% of the high expansion particles are greater than about 500 micrometers.
9. The gypsum core according to claim 5 , wherein at least 80% to about 95% of the high expansion particles are greater than about 500 micrometers.
10. The gypsum core according to claim 5 , wherein between about 35% and 60% of the high expansion particles are between about 500 micrometers and about 1000 micrometers.
11. The gypsum core according to claim 5 , wherein between about 40% and 60% of the high expansion particles are between about 500 micrometers and about 1000 micrometers.
12. The gypsum core according to claim 5 , wherein between about 20% and about 40% of the high expansion particles are between about 1000 micrometers and about 1500 micrometers.
13. The gypsum core according to claim 5 , wherein the high expansion particles are high expansion vermiculite particles.