Polyamide molding compounds for hypochlorite-resistant applications

1. A molded body that is resistant to an aqueous solution comprising hypochlorous acid and/or a salt thereof, comprising:

at least one semi-crystalline polyamide (A) selected from the group consisting of PA MXD6, PA MXD10, PA 6T/6I, PA 9T/MODT wherein MOD stands for 2-methyl-1,8-octanediamine, PA 10T, PA 10T/6T, PA 10T/6T/10I/6I, PA 12T, PA 10T/10I, PA 6T/6, PA 6T/66, PA 10T/6T/1012/612, PA 6T/BACT, PA 66/BAC6/MACM6, PA 66/BAC6/PACM6, PA 66/BAC6/IPD6 and copolymers thereof and

at least one amorphous or microcrystalline polyamide (B) selected from the group consisting of PA MACMI/MACM12, PA MACMT/MACM12, PA 6I/MACMI/12, PA MACMT/MACM36, PA MACMI/MACMT/MACM36, PA 6I/6T/MACMI/MACMT, PA 6I/6T/MACMI/MACMT/MACM12/612, PA 6I/6T/MACMI/MACMT/MACM12, PA MACMI/MACMT/MACM12/12, PA MACMI/MACMT/MACM12, PA MACMI/MACMT/MACM12/MACM36, PA MXDI/6I, PA MXDI/MXD6, PA MACM36, PA MACM10/1010, PA MACM14/1014, and copolymers thereof,

wherein, when MACM accounts for up to 35 mol % of all monomers before replacement, MACM can be partially or fully replaced by PACM and/or TMDC, keeping the sum of the molar fractions of all monomers at 100 mol %, or when MACM accounts for more than 35 mol % of all monomers before replacement, MACM can be replaced by PACM and/or TMDC such that the replaced amount of MACM does not exceed 35 mol %, keeping the sum of the molar fractions of all monomers at 100 mol %, and/or

laurin lactam can be replaced entirely or partially with caprolactam, and/or

the dimeric fatty acid having 36 carbon atoms can be replaced entirely or partially with a dimeric fatty acid having 44 carbon atoms,

and

optionally at least one further compound selected from the group consisting of inorganic filler (C), one or more additives (D) selected from the group consisting of inorganic and organic stabilizers, lubricants, dyes, marking agents, pigments, carbon black, graphite, graphene, carbon nanotubes, photochromic agents, antistatic agents, release agents, anti-block additives, chain-extending additives, chain-shortening additives, optical brighteners, IR absorbers, and NIR absorbers, and a polymer (E) which is different from polyamide (A), polyamide (B), and additive (D).

2. The molded body to claim 1 , which is selected from the group consisting of components for the delivery and/or storage of drinking water or warm water, faucets, fittings, housings, mixers, taps, filter housings, water meters, water meter components, valves, valve components, water distributors, cartridges, pumps, pump components, viewing glasses, covers, water lines, and receptacles.

3. The molded body according to claim 1 , wherein the at least one amorphous or microcrystalline polyamide (B) has a glass transition temperature, measured according to ISO 11537-2 (2013), of 60 to 240° C.

4. The molded body according to claim 1 , wherein the polyamide molding compound additionally comprises at least one of the following components selected from the group consisting of an inorganic filler (C), an additive (D), and a further polymer (E) that is different from polyamide (A), polyamide (B), and additive (D).

5. The molded body according to claim 1 , wherein the polyamide molding compound comprises at least one inorganic filler (C) selected from the group consisting of fibrous fillers and needle-shaped fillers.

6. The molded body according to claim 1 , wherein the polyamide molding compound comprises at least one inorganic filler (C) selected from the group consisting of glass fibers and carbon fibers.

7. The molded body according to claim 1 , wherein the polyamide molding compound has the following composition:

19 to 95 wt. % of at least one semi-crystalline polyamide (A);

5 to 60 wt. % of at least one amorphous or microcrystalline polyamide (B);

0 to 70 wt. % of at least one inorganic filler (C);

0 to 6 wt. % at least one additive (D); and

0 to 20 wt. % of at least one polymer (E),

components (A) to (E) adding up to 100 wt. %.

8. The molded body according to claim 7 , wherein the polyamide molding compound has the following composition:

to 89.39 wt. % of at least one semi-crystalline polyamide (A);

to 50 wt. % of at least one amorphous or microcrystalline polyamide (B);

0.1 to 60 wt. % of at least one inorganic filler (C);

0.01 to 5 wt. % of at least one additive (D); and

0.5 to 15 wt. % of at least one polymer (E),

components (A) to (E) adding up to 100 wt. %.

9. The molded body according to claim 1 , wherein the polyamide molding compound comprises at least one inorganic filler (C) and at least one additive (D).

10. The molded body according to claim 9 , wherein the polyamide molding compound has the following composition:

19 to 95 wt. % of at least one semi-crystalline polyamide (A);

to 60 wt. % of at least one amorphous or microcrystalline polyamide (B);

0.1 to 70 wt. % of at least one inorganic filler (C); and

0.01 to 6 wt. % of at least one additive (D),

components (A) to (D) adding up to 100 wt. %.

11. The molded body according to claim 1 , wherein semi-crystalline polyamide (A) is selected from the group consisting of PA MXD6, PA MXD10, PA 9T/MODT wherein MOD stands for 2-methyl-1,8-octanediamine, PA 10T, PA 10T/6T, PA 10T/6T/101161, PA 12T, PA 10T/10I, PA 6T/6, PA 6T/66, PA 10T/6T/1012/612, PA 6T/BACT, PA 66/BAC6/MACM6, PA 66/BAC6/PACM6, PA 66/BAC6/IPD6, and copolymers thereof.

12. The molded body according to claim 1 , wherein the one or more additives (D) are selected from the group consisting of UV stabilizers, UV absorbers, UV blockers, lubricants, dyes, carbon black, graphite, graphene, carbon nanotubes, photochromic agents, antistatic agents, release agents, anti-block additives, chain-extending additives, chain-shortening additives, optical brighteners, IR absorbers, and NIR absorbers.

13. The molded body according to claim 1 , wherein the inorganic fillers (C) are selected from the group consisting of basalt fibers, boron fibers, slag fibers, metal fibers, wollastonite, aramide fibers, and combinations thereof.