Welded advanced high strength steel
This disclosure relates to weldability of steel alloys that provide weld joints which retain hardness values in a heat affected zone adjacent to a fusion zone and which also have improved resistance to liquid metal embrittlement due to the presence of zinc coatings.
1. A welded high strength steel sheet comprising 70 to 90 atomic % iron, one or both of Ni in an amount of from 0.4 to 11.6 at. % and Cu in an amount of from 0.4 to 2.8 at. %, and at least two elements selected from Si in an amount of from 0.7 to 6.5 at. %, Mn in an amount of from 0.8 to 16.0 at. %, Cr in an amount of from 0.4 to 8.8 at. % and C in an amount of from 0.4 to 3.8 at. %, wherein the steel sheet has a thickness of up to 5 mm, a total elongation of from 10.0 to 75.0%, a yield strength of from 250 to 1200 MPa, a tensile strength of from 700 to 1700 MPA, and a hardness H 1 , and wherein the steel sheet includes a weld zone comprising: a fusion zone containing >50 volume % austenite; and a heat affected zone having a hardness H 2 , wherein H 2 =H 1 +/−100 HV.
2. The welded high strength steel sheet of claim 1 , wherein the steel sheet has a thickness of from 0.1 mm to 5 mm.
3. The welded high strength steel sheet of claim 1 , wherein H 1 is from 150 to 650 HV.
4. The welded high strength steel sheet of claim 1 , wherein the steel sheet contains both Ni and Cu.
5. The welded high strength steel sheet of claim 1 , wherein the weld zone is a resistance spot weld, a resistance seam weld, an upset weld, a laser beam weld, or an electron beam weld.
6. The welded high strength steel sheet of claim 1 , wherein at least a portion of the steel sheet is coated with a zinc-containing coating.
7. The welded high strength steel sheet of claim 1 , wherein the weld zone is a side-by-side weld between the high strength steel sheet and another steel sheet.
8. The welded high strength steel sheet of claim 7 , wherein the other steel sheet is of a same grade as the high strength steel sheet.
9. The welded high strength steel sheet of claim 7 , wherein the other steel sheet is of a different grade than a grade of the high strength steel sheet.