Method for manufacturing metal oxynitride film
View Patent ↗A method for depositing a metal oxynitride film by epitaxial growth at a low temperature is provided. It is a method for manufacturing a metal oxynitride film, in which the metal oxynitride film is epitaxially grown on a single crystal substrate by a sputtering method using an oxide target with a gas containing a nitrogen gas introduced. The oxide target contains zinc, the substrate during the deposition of the metal oxynitride film is higher than or equal to 80° C. and lower than or equal to 400° C., and the flow rate of the nitrogen gas is greater than or equal to 50% and lower than or equal to 100% of the total flow rate of the gas.
1. A method for manufacturing a metal oxynitride film,
wherein the metal oxynitride film is epitaxially grown in contact with a single crystal substrate by a sputtering method using an oxide target with a gas containing a nitrogen gas introduced,
wherein the oxide target comprises zinc,
wherein the single crystal substrate during deposition of the metal oxynitride film has a temperature that is higher than or equal to 80° C. and lower than or equal to 400° C., and
wherein a flow rate of the nitrogen gas is greater than or equal to 50% and lower than or equal to 100% of a total flow rate of the gas.
2. The method for manufacturing a metal oxynitride film, according to claim 1 ,
wherein the oxide target comprises at least one of the group of indium and gallium.
3. The method for manufacturing a metal oxynitride film, according to claim 1 ,
wherein the single crystal substrate is an yttria-stabilized zirconia (YSZ) substrate, and
wherein a plane orientation of the single crystal substrate is (111).
4. The method for manufacturing a metal oxynitride film, according to claim 1 ,
wherein the single crystal substrate is an A-plane sapphire substrate, and
wherein a plane orientation of the single crystal substrate is (110).
5. The method for manufacturing a metal oxynitride film, according to claim 1 ,
wherein a crystal structure of the metal oxynitride film is a wurtzite structure.
6. The method for manufacturing a metal oxynitride film, according to claim 5 ,
wherein when pole measurement is performed on the metal oxynitride film, a diffraction peak indicating six-fold symmetry is observed in a φ scan on a (101) plane of a crystal of the metal oxynitride film in the pole measurement.
7. The method for manufacturing a metal oxynitride film, according to claim 6 ,
wherein a first spot and a second spot are observed in a wide-angle reciprocal space map of the metal oxynitride film,
wherein a peak of the first spot is positioned at an angle 2θ of greater than or equal to 30° and less than or equal to 35° and an angle of around 0°,
wherein a half-width of the first spot is less than 2°,
wherein a peak of the second spot is positioned at an angle 2θ of greater than or equal to 33° and less than or equal to 37° and an angle of greater than or equal to 61° and less than or equal to 65°, and
wherein a half-width of the second spot is less than 2°.
8. A method for manufacturing an in-plane oriented metal oxynitride film,
wherein an in-plane oriented metal oxynitride film is deposited in contact with a single crystal substrate by a sputtering method using an oxide target with a gas containing a nitrogen gas introduced,
wherein the oxide target comprises zinc,
wherein the single crystal substrate during deposition of the in-plane oriented metal oxynitride film has a temperature that is higher than or equal to 80° C. and lower than or equal to 400° C., and
wherein a flow rate of the nitrogen gas is greater than or equal to 50% and lower than or equal to 100% of a total flow rate of the gas.
9. The method for manufacturing an in-plane oriented metal oxynitride film, according to claim 8 ,
wherein the oxide target comprises at least one of the group of indium and gallium.
10. The method for manufacturing an in-plane oriented metal oxynitride film, according to claim 8 ,
wherein the single crystal substrate is an yttria-stabilized zirconia (YSZ) substrate, and
wherein a plane orientation of the single crystal substrate is (111).
11. The method for manufacturing an in-plane oriented metal oxynitride film, according to claim 8 ,
wherein the single crystal substrate is an A-plane sapphire substrate, and
wherein a plane orientation of the single crystal substrate is (110).
12. The method for manufacturing an in-plane oriented metal oxynitride film, according to claim 8 ,
wherein a crystal structure of the in-plane oriented metal oxynitride film is a wurtzite structure.
13. The method for manufacturing an in-plane oriented metal oxynitride film, according to claim 12 ,
wherein when pole measurement is performed on the in-plane oriented metal oxynitride film, a diffraction peak indicating six-fold symmetry is observed in a φ scan on a (101) plane of a crystal of the in-plane oriented metal oxynitride film in the pole measurement.
14. The method for manufacturing an in-plane oriented metal oxynitride film, according to claim 13 ,
wherein a first spot and a second spot are observed in a wide-angle reciprocal space map of the in-plane oriented metal oxynitride film,
wherein a peak of the first spot is positioned at an angle 2θ of greater than or equal to 30° and less than or equal to 35° and an angle of around 0°,
wherein a half-width of the first spot is less than 2°,
wherein a peak of the second spot is positioned at an angle 2θ of greater than or equal to 33° and less than or equal to 37° and an angle ψ of greater than or equal to 61° and less than or equal to 65°, and
wherein a half-width of the second spot is less than 2°.