Method for producing alcohol and catalyst for producing alcohol
A method and catalyst for producing an alcohol, which method includes supplying water and a C2-C5 olefin to a reactor and performing hydration in a gas phase using a solid acid catalyst. The solid acid catalyst is one in which a heteropolyacid or a salt thereof is supported on a silica carrier. The silica carrier is obtained by kneading a fumed silica obtained by a combustion method, a silica gel obtained by a gel method, and a colloidal silica obtained by a sol-gel method or a water glass method; molding the resulting kneaded product; and calcining the resulting molded body.
1. A method for producing an alcohol comprising
kneading a fumed silica obtained by a combustion method, a silica gel obtained by a gel method, and a colloidal silica obtained by a sol-gel method or a water glass method,
forming the obtained kneaded material, and
then calcining the obtained shaped body to form a silica carrier,
supporting a heteropolyacid or a salt thereof on the silica carrier to form a solid acid catalyst, and
supplying water and an olefin having 2 to 5 carbon atoms to a reactor filled with the solid acid catalyst and subjecting them to a hydration reaction in a gas phase,
wherein a blending amount of the fumed silica is 5 to 50 parts by mass, a blending amount of the silica gel is 40 to 90 parts by mass, and a blending amount of a solid content of the colloidal silica is 5 to 30 parts by mass, based on total parts by mass of the silica carrier.
2. The method for producing an alcohol according to claim 1 , wherein the calcining temperature is 300 to 1000° C.
3. The method for producing an alcohol according to claim 1 , wherein the heteropolyacid is at least one compound selected from the group consisting of silicotungstic acid, phosphotungstic acid, phosphomolybdic acid, silicomolybdic acid, silicovanadotungstic acid, phosphovanadotungstic acid, and phosphovanadomolybdic acid.
4. The method for producing an alcohol according to claim 1 , wherein the silica carrier has mesopores having a pore diameter of 2 to 50 nm and macropores having a pore diameter of more than 50 nm and not more than 1000 nm in a pore diameter distribution measurement.
5. The method for producing an alcohol according to claim 4 , wherein in the pore diameter distribution by the mercury intrusion method, the pore volume of the macropores of the silica carrier is 0.05 to 0.50 cc/g.
6. The method for producing an alcohol according to claim 4 , wherein the BET specific surface area of the silica carrier is 200 to 500 m 2 /g.
7. The method for producing an alcohol according to claim 4 , wherein the bulk density of the silica carrier is 300 to 750 g/L.
8. The method for producing an alcohol according to claim 4 , wherein the average pore diameter of the mesopores of the silica carrier by the BJH method is 3 to 16 nm.
9. The method for producing an alcohol according to claim 4 , wherein the particle diameter of the silica carrier is 0.5 to 12 mm.
10. The method for producing an alcohol according to claim 4 , wherein the heteropolyacid is at least one compound selected from the group consisting of silicotungstic acid, phosphotungstic acid, phosphomolybdic acid, silicomolybdic acid, silicovanadotungstic acid, phosphovanadotungstic acid, and phosphovanadomolybdic acid.
11. The method for producing an alcohol according to claim 4 , wherein the olefin having 2 to 5 carbon atoms is ethylene and the alcohol produced by the hydration reaction is ethanol.
12. The method for producing an alcohol according to claim 11 , wherein an ether compound by-produced by the hydration reaction of ethylene is recycled into the reactor.