Topical skin closure compositions and systems
Novel compositions and systems for closure of wounds are disclosed. The compositions provide devices of improved flexibility and elasticity and are readily applied to wound sites or over wound closure devices. The present invention is also directed to a novel platinum catalyst for use in such compositions. The catalyst provides for rapid curing on topical surfaces such as skin and bonds to such surfaces in about 2-5 minutes.
1. A composition comprising:
a cross-linkable silicone polymer having reactive functionalities;
a silica-containing composition;
a silicone cross-linking agent; and,
a catalyst, wherein said catalyst comprises a platinum tetramethyldivinyl disiloxane diethyl maleate complex having the formula:
Pt [( CH 2= CH )( CH 3)2 Si] 2 O ·(COCH=CHCO)( C 2 H 5 O )2,
wherein the composition comprises the combination of equal volumes of a Part A and a Part B, wherein:
Part A comprises 85 to 95 wt. % vinyl terminated polydimethyl silicone base polymer and fumed silica particles, 5 to 15 wt. % vinyl terminated polydimethylsiloxane having a molecular weight ranging from 3,000 to 9,000 and containing 100 to 250 ppm of elemental platinum contributed from the catalyst Pt[(CH 2 =CH)(CH 3 ) 2 Si] 2 O·(COCH=CHCO)(C 2 H 5 O) 2 ; and
Part B comprises 60 to 80 wt. % vinyl terminated polydimethyl silicone base polymer and fumed silica particles, 10 to 37 wt. % polymethylhydro-co-polydimethyl siloxane cross linker, and 3 to 12 wt. % hydride terminated polydimethylsiloxane having a molecular weight ranging from 3,000 to 9,000.
2. The composition of claim 1 , wherein the cross-linkable silicone polymer is selected from the group consisting of vinyl terminated polydialkylsiloxane, vinyl terminated polydimethylsiloxane, vinyl terminated polydiphenylsilane-dimethylsiloxane copolymer, vinyl terminated polyphenylmethylsiloxane, vinyl terminated polyfluoropropylmethyl-dimethylsiloxane copolymer, vinyl terminated polydiethylsiloxane, and SiH terminated polydimethyldisiloxane.
3. The composition of claim 1 , wherein the cross-linkable silicone polymer comprises vinyl terminated polydimethylsiloxane.
4. The composition of claim 1 , wherein the silica-containing composition comprises a trimethyl silyl surface treated silica filler.
5. The composition of claim 1 , wherein the silica-containing composition is selected from the commercially available reactive silica-containing silicone bases including HCR (high consistent rubber) bases and LSR (liquid silicone rubber) bases.
6. The composition of claim 5 , wherein the silica-containing composition is a liquid silicone rubber base.
7. The composition of claim 1 , wherein the silicone cross-linking agent is selected from the group consisting of polymethylhydrosiloxane, polymethylhydro-co-polydimethylsiloxane, polyethyhydrosiloxane, polymethylhydrosiloxane-co-octylmethylsiloxane, and polymethylhydrosiloxane-co-methylphenylsiloxane.
8. The composition of claim 1 , wherein the silicone cross-linking agent comprises polymethylhydrosiloxane, polymethylhydro-co-polydimethylsiloxane and combinations thereof.
9. The composition of claim 1 , wherein the composition additionally comprises about 0 wt. % to about 30 wt. % of an organic solvent, based upon the weight of the composition.
10. The composition of claim 1 , wherein the composition comprises about 1 wt. % to about 15 wt. % of the silicone cross-linking agent based on total solids, wherein the coating composition additionally comprises about 0 wt. % to about 30 wt. % of an organic solvent, based upon the weight of the coating composition.
11. The composition of claim 1 , wherein the coating composition comprises about 0.003 wt. % to about 0.06 wt. % of the platinum catalyst, based on total solids, wherein the coating composition additionally comprises about 0 wt. % to about 30 wt. % of an organic solvent, based upon the weight of the coating composition.
12. The composition of claim 1 , wherein the coating composition additionally comprises a solvent selected from the group consisting of pentane, hexane, heptanes, mixtures of low molecular weight olefins, and combinations thereof.
13. The coating composition of claim 1 , wherein the composition is curable at temperatures at about 19° C.
14. The coating composition of claim 13 , wherein the composition is curable at temperatures of about 28° C. in about 2-5 minutes.
15. A kit comprising:
a) a wound closure device; and
b) the composition of claim 1 .
16. The kit of claim 15 , wherein the wound closure device is a wound closure strip.
17. The kit of claim 16 , wherein the wound closure strip is selected from the group consisting of meshes, polymeric films, plastic foams, woven fabrics, knitted fabrics, a non-woven fabrics and combinations thereof.
18. The kit of claim 17 , wherein the wound closure strip is a mesh.
19. The kit of claim 18 , wherein the wound closure device comprises materials selected from the group consisting of polyesters, nylons, acrylics, rayons, polyurethanes, polyurethane foams, polystyrenes, polyesters, polyethylene terephthalate (PET), polyamides, polylactic acids, polyglycolic acids, polycaprolactones, and mixtures thereof; cotton, silk and linen; and surface-treated materials that impart an OH functionality to their surfaces.
20. A composition comprising:
a cross-linkable silicone polymer having reactive functionalities;
a silica-containing composition;
a silicone cross-linking agent; and,
a catalyst, wherein said catalyst comprises a platinum tetramethyldivinyl disiloxane diethyl maleate complex having the formula:
Pt [( CH 2= CH )( CH 3)2 Si] 2 O ·(COCH=CHCO)( C 2 H 5 O )2,
wherein the composition comprises the combination of equal volumes of a Part A and a Part B, wherein:
Part A comprises 30-100 wt. % vinyl terminated polydimethyl silicone base polymer and fumed silica particles, 5 to 15 wt. % vinyl terminated polydimethylsiloxane having a molecular weight ranging from 3,000 to 9,000 and containing 100 to 250 ppm of elemental platinum contributed from the catalyst Pt[(CH 2 =CH)(CH 3 ) 2 Si] 2 O·(COCH=CHCO)(C 2 H 5 O) 2 ; and
Part B comprises 0 to 30 wt. % vinyl terminated polydimethyl silicone base polymer and fumed silica particles, 10 to 40 wt. % polymethylhydro-co-polydimethyl siloxane cross linker, and 3 to 12 wt. % hydride terminated polydimethylsiloxane having a molecular weight ranging from 3,000 to 9,000.
21. A composition comprising:
a cross-linkable silicone polymer having reactive functionalities;
a silica-containing composition;
a silicone cross-linking agent; and,
a catalyst, wherein said catalyst comprises a platinum tetramethyldivinyl disiloxane diethyl maleate complex having the formula:
Pt [( CH 2= CH )( CH 3)2 Si] 2 O ·(COCH=CHCO)( C 2 H 5 O )2,
wherein the composition comprises the combination of equal volumes of a Part A and a Part B, wherein:
Part A comprises 0 to 40 wt. % vinyl terminated polydimethyl silicone base polymer and fumed silica particles, 5 to 15 wt. % vinyl terminated polydimethylsiloxane having a molecular weight ranging from 3,000 to 9,000 and containing 100 to 250 ppm of elemental platinum contributed from the catalyst of Pt[(CH 2 =CH)(CH 3 ) 2 Si] 2 O·(COCH=CHCO)(C 2 H 5 O) 2 ; and
Part B comprises 70-100 wt. % vinyl terminated polydimethyl silicone base polymer and fumed silica particles, 10 to 40 wt. % polymethylhydro-co-polydimethyl siloxane cross linker, and 3 to 12 wt. % hydride terminated polydimethylsiloxane having a molecular weight ranging from 3,000 to 9,000.